SABIC HDPE M200056 产品说明：
SABIC® HDPE M200056 is a high density polyethylene copolymer injection moulding grade with a narrow molecular weight distribution. It is typically used for easy mold fill-out and low warpage with a good balance of toughness and stiffness characteristics.
Typical applications.
SABIC® HDPE M200056 is typically used for injection moulding of food containers, housewares, toys, base cups, caps and closures.
This product is not intended for and must not be used in any pharmaceutical/medical applications.
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.956 | g/cm3 | ISO 1183 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| 抗环境应力开裂 1(60°C, 3.00 mm, Rhodacal-DS10, 模压成型) | 60.0 | hr | 内部方法 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D, 模压成型) | 62 | ISO 868 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 (2.00 mm, 模压成型) | 1200 | MPa | ISO 527-2/1BA/50 |
| 抗张强度 2 | ASTM D638 | ||
| 屈服, 2.00 mm, 模压成型 | 28.0 | MPa | ASTM D638 |
| 断裂, 2.00 mm, 模压成型 | 15.0 | MPa | ASTM D638 |
| 伸长率 3(断裂, 2.00 mm, 模压成型) | > 200 | % | ASTM D638 |
| 弯曲模量 (2.00 mm, 模压成型) | 1350 | MPa | ISO 178 |
| 弯曲应力 (2.00 mm, 模压成型) | 28.0 | MPa | ISO 178 |
HDPE特性：
高密度聚乙烯具有良好的耐热性和耐寒性，化学稳定性好，还具有较高的刚性和韧性，机械强度好。介电性能，耐环境应力开裂性亦较好。硬度、拉伸强度和蠕变性优于低密度聚乙烯；耐磨性、电绝缘性、韧性及耐寒性均较好，但与低密度绝缘性比较略差些；化学稳定性好，在室温条件下，不溶于任何有机溶剂，耐酸、碱和各种盐类的腐蚀；薄膜对水蒸气和空气的渗透性小、吸水性低；耐老化性能差，耐环境开裂性不如低密度聚乙烯，特别是热氧化作用会使其性能下降，所以，树脂需加入抗氧剂和紫外线吸收剂等来提高改善这方面的不足。高密度聚乙烯薄膜在受力情况下的热变形温度较低，这一点应用时要注意。
应用：用于挤出包装薄膜，绳索，编织袋，渔网，水管；注塑低档日用品及外壳，非承载荷构件，胶箱，周转箱；挤出吹塑容器，中空制品，瓶子。