SABIC HDPE ICP5505 产品说明：

SABIC® HDPE ICP5505 is part of SABIC's new breakthrough high density polyethylene Industial Container Product portfolio. The grade meets latest market expectations regarding property balance and processing behaviour.

SABIC® HDPE ICP5505 is typically used for state of the art blow moulding UN approved Open Head drums, from 25 up to 220 liter and more. This food approved grade is also very suited for the production of UN approved Jerry Cans. It combines excellent rigidity and impact with optimal stress crack resistance and easy processing performance, which offers potential system cost reduction.

The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications.

物理性能	额定值	单位制	测试方法
密度	0.955	g/cm3	ISO 1183
熔流率（熔体流动速率） (190°C/21.6 kg)	5.0	g/10 min	ISO 1133

硬度	额定值	单位制	测试方法
肖氏硬度 (邵氏 D, 23°C, 模压成型)	62		ISO 868

机械性能	额定值	单位制	测试方法
拉伸模量 (23°C, 2.00 mm, 模压成型)	1100	MPa	ISO 527-2/1BA/50
拉伸应力			ISO 527-2/1BA/50
屈服, 23°C, 2.00 mm, 模压成型	26.0	MPa	ISO 527-2/1BA/50
断裂, 23°C, 2.00 mm, 模压成型	40.0	MPa	ISO 527-2/1BA/50
拉伸应变 (断裂, 23°C, 2.00 mm, 模压成型)	> 1000	%	ISO 527-2/1BA/50
弯曲模量 (23°C, 2.00 mm, 模压成型)	1300	MPa	ISO 178
弯曲应力 (23°C, 2.00 mm, 模压成型)	27.0	MPa	ISO 178
ESCR (Strain Hardening) - Gp	17.0	MPa	内部方法

热性能	额定值	单位制	测试方法
Enthalpy Change	207	J/g	ISO 11357-3

SABIC HDPE ICP5505

基本特性：高密度聚乙烯是一种不透明白色腊状材料，比重比水轻，比重为0.941~0.960，柔软而且有韧性，但比LDPE略硬，也略能伸长，无毒，无味

。

燃烧特性：易燃，离火后能继续燃烧，火焰上端呈黄色，下端呈蓝色，燃烧时会熔融，有液体滴落，无黑烟冒出，同时，发出石蜡燃烧时发出的气味。

主要优点：耐酸碱，耐有机溶剂，电绝缘性优良，低温时，仍能保持一定的韧性。表面硬度，拉伸强度，刚性等机械强度都高于LDPE，接近于PP，比PP韧，但表面光洁度不如PP。

主要缺点：机械性能差，透气差，易变形，易老化，易发脆，脆性低于PP，易应力开裂，表面硬度低，易刮伤。难印刷，印刷时，需进行表面放电处理，不能电镀，表面无光泽。

主要用途：

高密度聚乙烯树脂可采用注射、挤出、吹塑和旋转成型等方法成型塑料制品。采用注射成型可成型出各种类型的容器、工业配件、医用品、玩具、壳体、瓶塞和护罩等制品。采用吹塑成型可成型各种中空容器、超薄型薄膜等。采用挤出成型可成型管材、拉伸条带、捆扎带、单丝、电线和电缆护套等。

另外，还可成型建筑用装饰板、百叶窗、合成木材、合成纸、合成膜和成型钙塑制品等   。

SABIC HDPE ICP5505 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！