SABIC HDPE F0863 产品说明：
SABIC® HDPE F0863 resin is a homopolymer with a very high density manufactured by gas phase technology. The grade offers high stiffness, high temperature resistance, low water vapour transmission and a very low gel level. Because of the linear character it is advisable to use the material in combination with extrusion coating LDPE grades like SABIC® LDPE 2005EC in order to improve extrusion coating processability (motorload and Neck In).
Application
SABIC® HDPE F0863 is typically used for food packaging, release paper and photographic paper.
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.964 | g/cm3 | ISO 1183 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 8.0 | g/10 min | ISO 1133 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 薄膜厚度 - 经测试 | 25 | μm | |
| 拉伸模量 | ISO 527-3 | ||
| MD : 25 μm, 铸造薄膜 | 580 | MPa | ISO 527-3 |
| TD : 25 μm, 铸造薄膜 | 580 | MPa | ISO 527-3 |
| 拉伸应力 | ISO 527-3 | ||
| MD : 屈服, 25 μm, 铸造薄膜 | 26.0 | MPa | ISO 527-3 |
| TD : 屈服, 25 μm, 铸造薄膜 | 24.0 | MPa | ISO 527-3 |
| MD : 断裂, 25 μm, 铸造薄膜 | 22.0 | MPa | ISO 527-3 |
| TD : 断裂, 25 μm, 铸造薄膜 | 18.0 | MPa | ISO 527-3 |
| 伸长率 | ISO 527-3 | ||
| MD : 断裂, 25 μm, 铸造薄膜 | 700 | % | ISO 527-3 |
| TD : 断裂, 25 μm, 铸造薄膜 | 800 | % | ISO 527-3 |
| 透氧率 (23°C, 25 μm, 铸造薄膜) | 0.100 | cm3/m2/24 hr | 内部方法 |
| 水气透过率 (38°C, 100% RH, 25 μm, 铸造薄膜) | 4.0 | g/m2/24 hr | 内部方法 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 维卡软化温度 | 130 | °C | ISO 306/A |
| 溶融温度（DSC） | 134 | °C | DIN 53765 |
| Enthalpy Change | 224 | J/g | DIN 53765 |
SABIC HDPE F0863
HDPE特性：
高密度聚乙烯具有良好的耐热性和耐寒性，化学稳定性好，还具有较高的刚性和韧性，机械强度好。介电性能，耐环境应力开裂性亦较好。硬度、拉伸强度和蠕变性优于低密度聚乙烯；耐磨性、电绝缘性、韧性及耐寒性均较好，但与低密度绝缘性比较略差些；化学稳定性好，在室温条件下，不溶于任何有机溶剂，耐酸、碱和各种盐类的腐蚀；薄膜对水蒸气和空气的渗透性小、吸水性低；耐老化性能差，耐环境开裂性不如低密度聚乙烯，特别是热氧化作用会使其性能下降，所以，树脂需加入抗氧剂和紫外线吸收剂等来提高改善这方面的不足。高密度聚乙烯薄膜在受力情况下的热变形温度较低，这一点应用时要注意。
应用：用于挤出包装薄膜，绳索，编织袋，渔网，水管；注塑低档日用品及外壳，非承载荷构件，胶箱，周转箱；挤出吹塑容器，中空制品，瓶子。