TPU Estane 5714 产品说明:
Type: Estane® 5714 is a Polyether Type Thermoplastic Polyurethane (TPU).
Features: Low Temperature Flexibility, Excellent Abrasion, Fungal, and Chemical Resistance, and Hydrolytic Stability. Adhesives can be applied from solution or extruded as a melt coating. The resin is lightly dusted with calcium stearate and contains UV stabilizer.
Uses: Various adhesive and fabric coating, magnetic media binder and cast films for lamination
物理性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
比重 | 1.11 | g/cm3 | ASTM D792 |
硬度 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
肖氏硬度 (邵氏 A) | 80 | ASTM D2240 |
机械性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
抗张强度 | ASTM D638 | ||
-- | 31.0 | MPa | ASTM D638 |
100% 应变 | 4.80 | MPa | ASTM D638 |
300% 应变 | 9.00 | MPa | ASTM D638 |
伸长率 (断裂, 0.762 mm) | 530 | % | ASTM D638 |
弹性体 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
拉伸应力 | ASTM D412 | ||
100%应变 | 4.80 | MPa | ASTM D412 |
300%应变 | 9.00 | MPa | ASTM D412 |
抗张强度 (断裂) | 31.0 | MPa | ASTM D412 |
伸长率 (断裂) | 530 | % | ASTM D412 |
热性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
玻璃转化温度 | -38.0 | °C | DSC |
维卡软化温度 | 71.0 | °C | ASTM D1525 |
Ring and Ball Softening Point | 174 | °C | ASTM E28-92 |
TPU Estane 5714
特性
1、耐磨性能
当材料在使用过程中经常受摩擦、刮磨、研挫等机械作用,会引起其表面逐步磨损,因此材料的选择磨耗性显得非常重要。
2、拉伸性能
拉伸强度高达70MPa ,断裂伸长率可高达1000%。
3、撕裂性能
弹性体在应用时由于产生裂口扩大而使之破坏称为撕裂,撕裂强度就是材料抵抗撕裂作用的能力;一般而言TPU具有较高的抗撕裂能力。
4、屈折性能
很多塑胶材料在重复的周期性应力作用下容易产生断裂,TPU制品在不同环境下都可以保持极佳的耐屈折特性,为高分子材料中最佳选择之一。
5、抗高温与抗氧化性能
一般的塑胶原料长期在70℃以上的环境下容易氧化,TPU抗氧化能力良好;一般而言TPU耐温性可达120℃。
6、低温性能
TPU有非常好的耐低温性能,通常能达到-50℃,可取代一般PVC因低温脆化而无法应用的各个领域,特别适合用在寒带相关的种类制品。
7、气密性
TPU非常容易利用高周波或是热压来熔接,因此广泛应用在充气制品上。气体系数是指在一定温度和压力下,气体透过试样规定面积的速率,同一材料对不同气体的透过率有时差异很大。一般来说,聚酯系列制品气密性比聚醚系列更好。
8、生物医学性能
TPU具有极佳的生物相容性、无毒、无过敏反应性、无局部刺激性、无致热源性,因此广泛应用在医疗、卫生等相关产品以及运动、保护器材上。
TPU塑胶原料应用范围
TPU已被广泛应用于:鞋材、成衣、充气玩具、水上及水下之运动器材、医疗器材、健身器材、汽车椅座材料、雨伞、皮箱、皮包等。
TPU薄膜在运动鞋上应用极广泛:鞋底及鞋面上的商标装饰、气囊、气垫、油包等。而今,TPU薄膜在运动鞋上应用又有两种趋势: