东莞市金韩塑胶有限公司
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 |
| 24小时吸水率 | ASTM D-570 | 0.3 | % | |
| 泰伯磨耗量 | H 18轮 | ASTM D-1044 | 47 | mg/1000rev |
| 比重 | ASTM D-792 | 1.25 | ||
| 泰伯磨耗量 | CS-17轮 | ASTM D-1044 | 13 | mg/1000rev |
| 熔体流动速率 | ASTM D-1238 | 12.5 | g/10min | |
| 硬度计硬度 | ASTM D-2240 | 72 | ||
| 断裂伸长 | ASTM D-638 | 360 | % | |
| 拉伸力(5%伸长) | ASTM D-638 | 14 | MPa | |
| 拉伸力(10%伸长) | ASTM D-638 | 20 | MPa | |
| 断裂拉伸力 | ASTM D-638 | 45.8 | MPa | |
| 埃佐冲击强度 | 23℃ | ASTM D-256 | 210 | J/m |
| 揉曲模量 | 23℃ | ASTM D-790 | 570 | MPa |
| 初耐撕裂性能 | ASTM D-1004 | 200 | kn/m | |
| 热畸变温度 | @0.5MPa | ASTM D-648 | 130 | ℃ |
| 维卡软化点 | ASTM D-1525 | 207 | ℃ | |
| 熔点 | ASTM D-3418 | 218 | ℃ | |
| 热畸变温度 | @0.18MPa | ASTM D-648 | 52 | ℃ |
| 耐揉曲切口增长性能 | ASTM D-1052 | >3×104 |