Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.38 g/cc | 0.0499 lb/in3 | ISO 1183 |
Water Absorption | 0.20 % | 0.20 % | ISO 62 |
Linear Mold Shrinkage, Flow | 0.020 cm/cm | 0.020 in/in | t = 3 mm |
Melt Flow | 10.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
10.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
Mechanical Properties | Metric | English | Comments |
Tensile Strength | 58.0 MPa | 8410 psi | 50 mm/min; ISO 527 |
Elongation at Break | 33 % | 33 % | 50 mm/min; ISO 527 |
Elongation at Yield | 10 % | 10 % | 50 mm/min; ISO 527 |
Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
Flexural Modulus | 2.40 GPa | 348 ksi | ISO 178 |
Charpy Impact, Notched | 0.650 J/cm2 | 3.09 ft-lb/in2 | ISO 179 |
POM KEPITAL FT2020
POM应用
.可代替大部分有色金属、汽车、机床、仪表内件、轴承、紧固件、齿轮、弹簧片、管道、运输带配件、电水煲、泵壳、沥水器、水龙头等.
一般性能
(1)POM是结晶型塑料,密度为1.42g/cm3,它的钢性很好,俗称“赛钢”.
(2)它具有耐疲劳、耐蠕变、耐磨、耐热、耐冲击等优良的性能,且摩擦系数小,自润滑性好.
(3)POM不易吸湿,吸水率为0.22~0.25%,在潮湿的环境中尺寸稳定性好,其收缩率为2.1%(较大),注塑时尺寸较难控制,热变形温度为172℃,聚甲醛有均聚甲醛两种,性能不同(均聚甲醛耐温性好一点).
力学性能
POM强度、刚度高,弹性好,减磨耐磨性好。其力学性能优异,比强度可达50.5MPa,比刚度可达2650MPa,与金属十分接近。POM的力学性能随温度变化小,共聚POM比均聚POM的变化稍大一点。POM的冲击强度较高,但常规冲击不及ABS和PC;POM对缺口敏感,有缺口可使冲击强度下降90%之多。POM的疲劳强度十分突出,10交变载荷作用后,疲劳强度可达35MPa,而PA和PC仅为28MPa。POM的蠕变性与PA相似,在20℃、21MPa、3000h时仅为2.3%,而且受温度的影响很小。POM的摩擦因数小,耐磨性好(POM>PA66>PA6>ABS>HPVC>PS>PC),极限PV值很大,自润滑性好。POM制品对磨时,高载荷作用时易产生类似尖叫的噪声。
电学性能
POM的电绝缘性较好,几乎不受温度和湿度的影响;介电常数和介电损耗在很宽的温度、湿度和频率范围内变化很小;耐电弧性极好,并可在高温下保持。POM的介电强度与厚度有关,厚度0.127mm时为82.7kV/mm,厚度为1.88mm时为23.6kV/mm。
POM环境性能
POM不耐强碱和氧化剂,对烯酸及弱酸有一定的稳定性。POM的耐溶剂性良好,可耐烃类、醇类、醛类、醚类、汽油、润滑油及弱碱等,并可在高温下保持相当的化学稳定性。吸水性小,尺寸稳定性好。