阻燃PA66 LEONA FR370 旭化成|价格|厂家|多少钱-全球塑胶网-移动端

PA66 LEONA.jpg

Physical Properties	Metric	English	Comments
Specific Gravity	1.16 g/cc	1.16 g/cc	Dry as Molded; ASTM D792
Density	1.16 g/cc	0.0419 lb/in3	Dry as Molded; ISO 1183
Moisture Absorption at Equilibrium	2.3 % @Temperature 23.0 °C	2.3 % @Temperature 73.4 °F	50% RH; ISO 62
	2.3 % @Temperature 23.0 °C	2.3 % @Temperature 73.4 °F	50% RH
Linear Mold Shrinkage, Flow	0.00900 - 0.0160 cm/cm	0.00900 - 0.0160 in/in	Asahi Kasei

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	55	55	Conditioned at 50% RH; ISO 2039
	85	85	Dry as Molded; ISO 2039
Hardness, Rockwell R	110	110	Conditioned at 50% RH; ISO 2039
	120	120	Dry as Molded; ISO 2039
Tensile Strength at Break	80.0 MPa	11600 psi	Conditioned at 50% RH; ISO 527
Tensile Strength	58.0 MPa	8410 psi	Conditioned at 50% RH; ASTM D638
	83.0 MPa	12000 psi	Dry as Molded; ASTM D638
Tensile Strength, Yield	55.0 MPa	7980 psi	Conditioned at 50% RH
	83.0 MPa	12000 psi	Dry as Molded
Elongation at Break	15 %	15 %	Dry as Molded; ISO 527
	>= 50.0 %	>= 50.0 %	Conditioned at 50% RH; ISO 527
Elongation at Yield	4.5 % @Temperature 23.0 °C	4.5 % @Temperature 73.4 °F	Dry as Molded; ISO 527
	22 % @Temperature 23.0 °C	22 % @Temperature 73.4 °F	Conditioned at 50% RH; ISO 527
Tensile Modulus	1.60 GPa	232 ksi	Conditioned at 50% RH; ISO 527
	3.60 GPa	522 ksi	Dry as Molded; ISO 527
Flexural Strength	54.1 MPa	7850 psi	Conditioned at 50% RH; ISO 178
	124 MPa	18000 psi	Dry as Molded; ISO 178
Flexural Modulus	1.50 GPa	218 ksi	Conditioned at 50% RH; ISO 178
	2.60 GPa	377 ksi	Dry as Molded; ISO 178
Izod Impact, Notched	0.290 J/cm	0.543 ft-lb/in	Dry as Molded; ASTM D256
	0.980 J/cm	1.84 ft-lb/in	Conditioned at 50% RH; ASTM D256
Charpy Impact Unnotched	5.80 J/cm2	27.6 ft-lb/in2	Dry as Molded; ISO 179
	NB	NB	Conditioned at 50% RH; ISO 179
Charpy Impact, Notched	0.400 J/cm2	1.90 ft-lb/in2	Dry as Molded; ISO 179
	0.600 J/cm2	2.86 ft-lb/in2	Conditioned at 50% RH; ISO 179

阻燃型
FR200	阻燃等级UL94 V-0；不含卤素和磷。	接头，开关，其他电气和电子材料。
FR370	阻燃等级UL94 V-0；不含卤素和磷。增强的抗焊接热性能。
FG170	玻璃纤维含量为15% GF; 阻燃等级UL94 V-0。
FG172	玻璃纤维含量为20% GF; 阻燃等级UL94 V-0。
FG173	玻璃纤维含量为30% GF; 阻燃等级UL94 V-0。