Panlite PC LV-2250Y 中等粘性 Teijin Kasei America, Inc. (Teijin Chemicals)

Panlite PC AD-5503 光学/镜头用途 Teijin Kasei America, Inc. (Teijin Chemicals)

Panlite PC B-4110R 10%碳纤增强 无卤阻燃级 高刚性 Teijin Kasei America, Inc. (Teijin Chemicals)

Panlite PC B-4120R 20%碳纤增强 无卤阻燃级 高刚性 Teijin Kasei America, Inc. (Teijin Chemicals)

Panlite PC B-4130R 30%碳纤增强 无卤阻燃级 高刚性 Teijin Kasei America, Inc. (Teijin Chemicals)

Panlite PC B-8110R 10%碳纤增强 高刚性 Teijin Kasei America, Inc. (Teijin Chemicals)

Panlite PC B-8120R 抗蠕变 20%碳纤增强 高刚性 Teijin Kasei America, Inc. (Teijin Chemicals)

Panlite PC B-8130R 30%碳纤增强 高刚性 Teijin Kasei America, Inc. (Teijin Chemicals)

Panlite PC BN-8110R 10%碳纤增强 阻燃级 高刚性 Teijin Kasei America, Inc. (Teijin Chemicals)

Panlite PC BN-8120R 20%碳纤增强 无卤阻燃级 高刚性 Teijin Kasei America, Inc. (Teijin Chemicals)

Panlite PC BS-8110R 10%碳纤增强 抗蠕变 高刚性 耐磨损 Teijin Kasei America, Inc. (Teijin Chemicals)

Panlite PC BS-8120R 20%碳纤增强 抗蠕变 高刚性 耐磨损 Teijin Kasei America, Inc. (Teijin Chemicals)

PC的生产方法：

商业上最重要的聚碳酸酯是以双酚A为原料，与光气反应或与碳酸二苯酯交换反应制成。

(1) 酯交换法

此法以双酚A和碳酸二苯酯为原料，分两步进行熔融缩聚，原理与涤纶生产相似。采用单体非等当量比，碳酸二苯酯过量进行端基封锁，排出苯酚以达到所需分子量。 

(2) 光气直接法

此法将双酚A钠盐的水溶液与光气的有机溶液进行界面缩聚直接合成。由于界面缩聚不可逆，并不要求严格等当量比。以胺类为催化剂。加少量单官能团酚进行端基封锁，控制分子量。

采用光气法制得的PC分子量（比用酯交换法）高。 

PC主要性能：

PC聚碳酸酯是透明的、微黄色或白色的刚硬而韧性的聚合物，密度为1.2g/cm3。分子量一般为2～10万，性能与分子量大小有关。PC的耐冲击性能，是热塑性塑料中最好的品种之一，比尼龙、聚甲醛高3～10倍，接近于酚醛和聚酯玻璃钢。PC具有良好的耐热性和耐低温性能，在较宽的温度范围内具有稳定的力学性能，尺寸稳定性，电性能和阻燃性，可在-60～120℃下长期使用；由于分子链刚性大，树脂熔体粘度大；吸水率小，收缩率小，尺寸精度高，尺寸稳定性好，薄膜透气性小；属自熄性材料；对光稳定，但不耐紫外光，耐候性好；耐油、耐酸、不耐强碱、氧化性酸及胺、酮类，溶于氯化烃类和芳香族溶剂。