导电 EMI /RFI屏蔽 PC/ABS NS0039 产品说明:
LNP* Faradex* NS0039 is a compound based on PC/ABS resin containing Flame Retardant, Stainless Steel. Added features of this material include: Electrically Conductive, EMI/RFI Shielding, Flame Retardant.
This data was supplied by SABIC-IP for the Americas region.
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 密度 | 1.35 g/cc | 0.0488 lb/in3 | ISO 1183 |
| 线性成型收缩率,Flow | 0.0042 cm/cm @Time 86400 sec |
0.0042 in/in @Time 24.0 hour |
ISO 294 |
| 线性成型收缩率，横向 | 0.0045 cm/cm @Time 86400 sec |
0.0045 in/in @Time 24.0 hour |
ISO 294 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 47.0 MPa | 6820 psi | ISO 527 |
| 抗张强度(屈服) | 58.0 MPa | 8410 psi | ISO 527 |
| 伸长率 (断裂) | 10 % | 10 % | ISO 527 |
| 屈服伸长率 | 3.3 % | 3.3 % | ISO 527 |
| 拉伸模量 | 3.20 GPa | 464 ksi | 1 mm/min; ISO 527 |
| 弯曲强度 | 102 MPa | 14800 psi | ISO 178 |
| 弯曲模量 | 3.40 GPa | 493 ksi | ISO 178 |
| 悬壁梁缺口冲击强度 | 6.00 kJ/m2 @Temperature 23.0 °C |
2.86 ft-lb/in2 @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| 悬壁梁无缺口冲击强度 | 43.0 kJ/m2 @Temperature 23.0 °C |
20.5 ft-lb/in2 @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 10000 ohm-cm | 10000 ohm-cm | ASTM D 257 |
| 表面电阻 | 1000 ohm | 1000 ohm | ASTM D 257 |
| Shielding Effectiveness | 50 - 65 dB @Thickness 3.00 mm |
50 - 65 dB @Thickness 0.118 in |
SABIC Method |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 77.0 μm/m-°C @Temperature -40.0 - 40.0 °C |
42.8 μin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 线性热膨胀系数,横向流动 | 64.0 μm/m-°C @Temperature -40.0 - 40.0 °C |
35.6 μin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 载荷下热变形温度(0.46 MPa) | 89.0 °C | 192 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 载荷下热变形温度(1.8 MPa) | 82.0 °C | 180 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 可燃性(UL94) | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
UL 94 by SABIC-IP |