PCTG TRITAN MP200 产品说明：

Eastman Tritan MP200 is an amorphous copolyester that combines excellent clarity and toughness with outstanding heat and chemical resistance. Film and sheet manufactured from this new-generation copolyester can be thermoformed with a wide processing window that allows for product designs that reflect intricate detail. Eastman Tritan MP200 copolyester is suitable for use with most forms of sterilization including radiation and ethylene oxide. It is NOT suitable for autoclave/steam sterilization. Eastman Tritan MP200 copolyester has been formulated for use in medical film, sheet, and packaging applications.

物理性能	额定值	单位制	测试方法
密度	1.19	g/cm3	ASTM D1505
吸水率 (24 hr)	0.50	%	ASTM D570

机械性能	额定值	单位制	测试方法
耐磨耗性 (23°C) 1	20% Haze		ASTM D1044

薄膜	额定值	单位制	测试方法
Carbon Dioxide Permeability (23°C, 254.0 μm)	210	cm3·mm/m2/atm/24 hr	ASTM D1434
PPT Tear Resistance			ASTM D2582
MD : 23°C, 254.0 μm	40	N	ASTM D2582
TD : 23°C, 254.0 μm	40	N	ASTM D2582
抗撕裂蔓延性			ASTM D1938
MD, Split Tear Method : 23°C, 254.0 μm	310	gf	ASTM D1938
TD, Split Tear Method : 23°C, 254.0 μm	200	gf	ASTM D1938

PCTG TRITAN MP200 

PCTG特性:

热成型性能

PCTG板材易于生产出造型复杂及拉伸比大的制品。而且，与PC板和抗冲改性的压克力不同，这种板材无须在热成型加工前进行预干燥处理。与PC板或压克力相比，其成型周期短，温度低，成品率更高。

坚韧性:

PCTG板材的挤出板材通常比通用压克力坚韧15至20倍，比抗冲改性的压克力坚韧5至10倍。PETG板材在加工、运输和使用过程中具有足够的承受能力，有助于防止破裂。

耐候性:

PCTG板材提供了优秀的耐候性。它可以保持产品的坚韧性，防止变黄。它含有紫外线吸收剂，可共挤成一保护层，保护了板材免受紫外线的有害影响。

加工简便:

PCTG板材可进行锯切、模切、钻孔、冲孔、剪切、铆接、铣边以及冷弯，不至于破碎。表面的轻微刮痕可用热风枪来消除。溶剂粘接亦是常规操作。它比通用压克力、抗冲改性压克力或PC板更易于加工，并可进行植绒、电镀、静电等加工处理。

优秀的耐化学性能

PCTG板材可以耐受多种化学品以及常用的清洁剂。

环保: PCTG板材基材均为环保材料，符合食品接触管理要求。

经济性: 比压克力经久耐用。

PCTG用途:

板、片材:

使用常规的成型方法，可以制备1~25.4mm厚的透明材料，具有突出的韧性和高抗冲击强度，其抗冲击强度是改性聚丙烯酸酯类的3~10倍，成型性能优异，冷弯曲不泛白，无裂纹，易于印刷和修饰，广泛应用于室内外标牌、储物架、自动售货机面板、家具、建筑及机械挡板等。

PCTG TRITAN MP200 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！