马来酸酐接枝SEBS美国科腾FG1901G 透明SEBS颗粒 涂层应用 密封剂 产品说明：

 

Kraton FG 聚合物是由马来酸酐(MA)接枝于中间链段的SEBS的 聚合物。市场上销售的Kraton FG 聚合物是接枝到共聚物上、重量为1.0-1.7％的马来酸酐。马来酸酐(MA)接枝提高了对于尼龙、聚酯、乙烯乙烯醇共聚物、铝、钢、玻璃和很多其他材料的粘结性

Kraton FG1901 G 是一个清晰的、线性triblock基于苯乙烯共聚物和乙烯/丁烯聚苯乙烯含量的30%。

 

Kraton FG1901 G作为沥青改性剂和聚合物。也适合在形成化合物鞋类应用和可用于制定粘合剂、密封剂和涂料。

 

马来酸酐接枝SEBS美国科腾FG1901G 透明SEBS颗粒 涂层应用 密封剂 物性表：

 

产品参数

 

KRATON? FG1901 G

苯乙烯-乙烯-丁烯-苯乙烯嵌段共聚物

Kraton Polymers LLC

产品说明:

Kraton FG1901 G is a clear, linear triblock copolymer based on styrene and ethylene/butylene with a polystyrene content of 30%. It is supplied from North America in the physical form identified below.

• FG1901 GT - supplied as a dusted pellet

Kraton FG1901 G is used as a modifier of bitumen and polymers. It is also suitable as an ingredient in formulating compounds for footwear applications and may be used in formulating adhesives, sealants, and coatings.

总体
材料状态	已商用：当前有效
资料1	Processing - KRATON D & G (English)Processing Guide (English)Technical Datasheet (English)
搜索 UL 黄卡	Kraton Polymers LLCKRATON?
供货地区	北美洲非洲和中东拉丁美洲欧洲亚太地区
特性	共聚物
用途	沥青改性密封剂塑料改性涂层应用鞋类粘合剂
外观	清晰/透明
形式	粒子

物理性能	额定值	单位制	测试方法
比重	0.910	g/cm3	ASTM D792
熔流率（熔体流动速率）(230°C/5.0 kg)	14 到 28	g/10 min	ASTM D1238
Maleic Anhydride Content - Bound	1.4 到 2.0	wt%	内部方法
含水量	< 500	ppm	内部方法
溶液粘度 - Toluene, 25%wt (25°C)	5.0	Pa·s	内部方法
硬度	额定值	单位制	测试方法
肖氏硬度(邵氏 A, 10 秒, 模压成型)	71		ASTM D2240

弹性体	额定值	单位制	测试方法
抗张强度(断裂)	34.5	MPa	ASTM D412
伸长率(断裂)	500	%	ASTM D412

补充信息	额定值
Styrene/Rubber ratio	30/70

 

 