东莞市新友塑胶有限公司
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 流动系数 | 200℃，10kg | ASTM D-1238 | 29.8 | g/10min | |
| 流动系数 | 200℃，5kg | ASTM D-1238 | 2.6 | g/10min | ||
| 物理性能 | 比重 | 23℃ | ASTM D-792 | 1.04 | ||
| 成型收缩率 | ASTM D-955 | 0.4-0.6 | % | |||
| 机械性能 | 硬度 | 1/2" | ASTM D-785 | 112 | R Scale | |
| 引张强度 | 降伏点 | 1/8",6mm/min | ASTM D-638 | 415 | kg/cm2(lb/in2) | |
| 破坏点 | 1/8",6mm/min | ASTM D-638 | 350 | kg/cm2(lb/in2) | ||
| 弯曲弹性率 | 1/4",2.8mm/min | ASTM D-790 | 22350 | kg/cm2 | ||
| 延伸率 | 1/8",6mm/min | ASTM D-638 | 70 | % | ||
| IZOD冲击强度 | 1/4",23℃ | ASTM D-256 | 27 | kg.cm/cm | ||
| 弯曲强度 | 1/4",2.8mm/min | ASTM D-790 | 610 | kg/cm2 | ||
| 热性能 | 维卡软化点 | 1/8",50℃/hr | ASTM D-1525 | 105 | ℃ | |
| 热变形温度 | 退火(85×8hr) | ASTM D-648 | 98 | ℃ | ||
| 线性膨胀系数 | TMA | 90×10-6 | mm/mm℃ | |||
| 燃烧率 | UL 94 | HB | 1/16" | |||
| 热变形温度 | 未退火 | ASTM D-648 | 85 | ℃ | ||
| 其它性能 | 耐光性 | △E(300hrs) | ASTM D-4459 | <1 | ||