美国陶氏/1410/吹塑级
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 熔体流动速率 | 190℃/2.16kg | ASTM D-1238 | 1.5 | g/10min |
| 熔体流动速率 | 190℃/2.16kg | ISO 1133 | 1.5 | g/10min | |
| 单体含量 | Internal Method | 9.7 | % | ||
| 物理性能 | 比重 | ASTM D-792 | 0.938 | g/cm3 | |
| 比重 | ISO 1183 | 0.938 | g/cm3 | ||
| 机械性能 | 拉伸屈服强度 | Compression Molded | ASTM D-638 | 8.39 | MPa |
| 拉伸屈服强度 | Compression Molded | ISO 527-2/508 | 8.39 | MPa | |
| 拉伸断裂强度 | Compression Molded | ASTM D-638 | 22.5 | MPa | |
| 拉伸断裂强度 | Compression Molded | ISO 527-2/508 | 22.5 | MPa | |
| 拉伸断裂伸长率 | Compression Molded | ASTM D-638 | 640 | % | |
| 拉伸断裂伸长率 | Compression Molded | ISO 527-2/508 | 640 | % | |
| 薄膜厚度-Tested | 50.8 | um | |||
| 拉伸屈服强度 | 50.8um | ASTM D-882 | |||
| MD | TD | ||||
| 11.8 | 10.9 | ||||
| MPa | |||
| 拉伸屈服强度 | 50.8um | ISO 527-3 | |
| TD | MD | ||
| 10.9 | 11.8 |
| MPa | |||
| 拉伸断裂强度 | 50.8um | ASTM D-882 | |
| TD | MD | ||
| 38.1 | 37.9 |
| MPa | |||
| 拉伸断裂强度 | 50.8um | ISO 527-3 | |
| MD | TD | ||
| 37.9 | 38.1 |
| MPa | |||
| 拉伸断裂伸长率 | 50.8um | ASTM D-882 | |
| TD | MD | ||
| 470 | 400 |
| % | |||
| 拉伸断裂伸长率 | 50.8um | ISO 527-3 | |
| MD | TD | ||
| 400 | 470 |
| % | ||||
| 落锤冲击 | 50.8um | ASTM D-1709B | 580 | g |
| 落锤冲击 | 50.8um | ISO 7765-1/B | 580 | g |
| 埃尔曼多夫撕裂强度 | 50.8um | ASTM D-1922 | ||
| TD | MD | |||
| 510 | 380 |
| g | |||
| 埃尔曼多夫撕裂强度 | 50.8um | ISO 6383-2 | |
| TD | MD | ||
| 2300 | 1700 |
| N | |||||
| 热性能 | 维卡软化点 | ASTM D-1525 | 81.1 | ℃ | |
| 维卡软化点 | ISO 306 | 81.1 | ℃ | ||
| 熔融温度 | Internal Method | 97.8 | ℃ | ||
| 光学性能 | 光泽度 | 45°，50.8um | ASTM D-2457 | 65 | |
| 雾度 | 50.8um | ISO 14782 | 5.8 | % | |
| 雾度 | 50.8um | ASTM D-1003 | 5.8 | % |