Ultramid® 8233G HS
聚酰胺6
33% 玻璃纤维增强材料
产品说明：
Ultramid 8233G HS is a heat stabilized, 33% glass fiber reinforced PA6 injection molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. It is also available in non-heat stabilized (Ultramid 8233G) and/or pigmented versions.
Applications
Ultramid 8233G HS is generally recommended for applications such as power tool housings, weed trimmer components, gears, automotive housings and under hood applications.
Ultramid® 8233G HS 物性表
| 基本信息 |
|
|
|
| 填料/增强材料 |
|
| 添加剂 |
|
| 特性 |
|
| 用途 |
草坪和园林设备 齿轮 动力/其它工具 汽车的发动机罩下的零件 汽车领域的应用 外壳 |
| 机构评级 |
|
| RoHS 合规性 |
|
| 外观 |
|
| 形式 |
|
| 加工方法 |
|
| 多点数据 |
Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2) |
| 物理性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 比重 |
1.39 |
-- |
g/cm3 |
ASTM D792, ISO 1183 |
| 收缩率 - 流动 (3.18 mm) |
0.30 |
-- |
% |
|
| 吸水率 |
|
|
|
|
| 24 hr |
1.1 |
-- |
% |
ASTM D570 |
| 23°C, 24 hr |
1.1 |
-- |
% |
ISO 62 |
| 饱和 |
6.4 |
-- |
% |
ASTM D570 |
| 饱和, 23°C |
6.4 |
-- |
% |
ISO 62 |
| 平衡, 50% RH |
1.8 |
-- |
% |
ASTM D570 |
| 平衡, 23°C, 50% RH |
1.8 |
-- |
% |
ISO 62 |
| 硬度 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 洛氏硬度 (R 级) |
121 |
-- |
|
ASTM D785 |
| 机械性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 拉伸模量 |
|
|
|
ISO 527-2 |
| -40°C |
10500 |
11600 |
MPa |
ISO 527-2 |
| 23°C |
10100 |
5840 |
MPa |
ISO 527-2 |
| 80°C |
4430 |
4300 |
MPa |
ISO 527-2 |
| 121°C |
3550 |
3400 |
MPa |
ISO 527-2 |
| 抗张强度 |
|
|
|
|
| 断裂, -40°C |
283 |
255 |
MPa |
ASTM D638, ISO 527-2 |
| 断裂, 23°C |
195 |
125 |
MPa |
ASTM D638 |
| 断裂, 80°C |
110 |
80.0 |
MPa |
ASTM D638, ISO 527-2 |
| 断裂, 121°C |
83.0 |
60.0 |
MPa |
ASTM D638, ISO 527-2 |
| 断裂, 23°C |
185 |
125 |
MPa |
ISO 527-2 |
| 伸长率 |
|
|
|
|
| 断裂, -40°C |
3.6 |
3.5 |
% |
ASTM D638 |
| 断裂, 23°C |
3.5 |
6.0 |
% |
ASTM D638, ISO 527-2 |
| 断裂, 80°C |
7.0 |
6.0 |
% |
ASTM D638 |
| 断裂, 121°C |
7.0 |
6.0 |
% |
ASTM D638 |
| 弯曲模量 |
|
|
|
|
| -40°C |
9830 |
10200 |
MPa |
ASTM D790 |
| 23°C |
9040 |
5130 |
MPa |
ASTM D790 |
| 65°C |
4020 |
-- |
MPa |
ASTM D790 |
| 90°C |
3750 |
-- |
MPa |
ASTM D790 |
| 121°C |
3320 |
-- |
MPa |
ASTM D790 |
| 23°C |
8200 |
5200 |
MPa |
ISO 178 |
| 弯曲强度 |
|
|
|
|
| -40°C |
380 |
361 |
MPa |
ASTM D790 |
| 23°C |
297 |
179 |
MPa |
ASTM D790 |
| 65°C |
160 |
-- |
MPa |
ASTM D790 |
| 90°C |
140 |
-- |
MPa |
ASTM D790 |
| 121°C |
112 |
-- |
MPa |
ASTM D790 |
| 23°C |
260 |
130 |
MPa |
ISO 178 |
| 冲击性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 简支梁缺口冲击强度 |
|
|
|
ISO 179 |
| -30°C |
10 |
-- |
kJ/m2 |
ISO 179 |
| 23°C |
15 |
-- |
kJ/m2 |
ISO 179 |
| 简支梁无缺口冲击强度 (23°C) |
88 |
-- |
kJ/m2 |
ISO 179 |
| 悬壁梁缺口冲击强度 |
|
|
|
|
| -40°C |
110 |
110 |
J/m |
ASTM D256 |
| 23°C |
150 |
240 |
J/m |
ASTM D256 |
| -40°C |
8.5 |
-- |
kJ/m2 |
ISO 180 |
| 23°C |
10 |
-- |
kJ/m2 |
ISO 180 |
| Drop Impact Resistance (23°C) |
4.07 |
6.78 |
J |
内部方法 |
| 热性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 载荷下热变形温度 |
|
|
|
|
| 0.45 MPa, 未退火 |
218 |
-- |
°C |
ASTM D648 |
| 0.45 MPa, 未退火 |
215 |
-- |
°C |
ISO 75-2/B |
| 1.8 MPa, 未退火 |
210 |
-- |
°C |
ASTM D648 |
| 1.8 MPa, 未退火 |
205 |
-- |
°C |
ISO 75-2/A |
| 熔融峰值温度 |
220 |
-- |
°C |
ASTM D3418, ISO 3146 |
| 线形热膨胀系数 |
|
|
|
|
| 流动 |
3.8E-5 |
-- |
cm/cm/°C |
ASTM E831 |
| 流动 |
2.1E-5 |
-- |
cm/cm/°C |
|
| 横向 |
7.0E-5 |
-- |
cm/cm/°C |
|
| RTI Elec |
|
|
|
UL 746 |
| 0.710 mm |
130 |
-- |
°C |
UL 746 |
| 1.50 mm |
140 |
-- |
°C |
UL 746 |
| 3.00 mm |
140 |
-- |
°C |
UL 746 |
| RTI Imp |
|
|
|
UL 746 |
| 0.710 mm |
115 |
-- |
°C |
UL 746 |
| 1.50 mm |
115 |
-- |
°C |
UL 746 |
| 3.00 mm |
120 |
-- |
°C |
UL 746 |
| RTI |
|
|
|
UL 746 |
| 0.710 mm |
130 |
-- |
°C |
UL 746 |
| 1.50 mm |
140 |
-- |
°C |
UL 746 |
| 3.00 mm |
140 |
-- |
°C |
UL 746 |
| 电气性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 体积电阻率 |
|
|
|
|
| 1.50 mm |
> 1.0E+13 |
-- |
ohms·cm |
ASTM D257 |
| -- |
> 1.0E+13 |
-- |
ohms·cm |
IEC 60093 |
| 介电强度 |
44 |
-- |
kV/mm |
IEC 60243-1 |
| 介电常数 |
|
|
|
IEC 60250 |
| 100 Hz |
4.20 |
-- |
|
IEC 60250 |
| 1 MHz |
3.60 |
-- |
|
IEC 60250 |
| 耗散因数 |
|
|
|
IEC 60250 |
| 100 Hz |
0.020 |
-- |
|
IEC 60250 |
| 1 MHz |
0.020 |
-- |
|
IEC 60250 |
| 可燃性 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| UL 阻燃等级 |
|
|
|
UL 94 |
| 0.600 mm |
HB |
-- |
|
UL 94 |
| 0.710 mm |
HB |
-- |
|
UL 94 |
| 1.50 mm |
HB |
-- |
|
UL 94 |
| 3.00 mm |
HB |
-- |
|
UL 94 |
| 注射 |
干燥 |
单位制 |
|
| 干燥温度 |
83.0 |
°C |
|
| 干燥时间 |
2.0 到 4.0 |
hr |
|
| 建议的最大水分含量 |
0.15 |
% |
|
| 加工（熔体）温度 |
270 到 295 |
°C |
|
| 模具温度 |
80.0 到 95.0 |
°C |
|
| 注塑压力 |
3.50 到 12.5 |
MPa |
|
| 注射速度 |
快速 |
|
|