产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 成型收缩率 | UBEmethod | 0.2 | % | |
| 成型收缩率 | UBEmethod | 0.7 | % | ||
| 吸水率 | ASTM D-570 | 6.6 | % | ||
| 物理性能 | 比重 | ASTM D-792 | 1.36 | ||
| 机械性能 | 弯曲弹性率 | 23° | ASTM D-790 | 80000 | kgf/cm2 |
| 断裂下的延伸率 | 23° | ASTM D-638 | 5 | % | |
| 抗冲击强度 | 23° | ASTM D-256 | 23 | kgf.cm/cm | |
| 1%变形下的压缩强度 | 23° | ASTM D-695 | 280 | kgf/cm2 | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 120 | ||
| 弯曲强度 | 23° | ASTM D-790 | 1300 | kgf/cm2 | |
| 屈服下的伸张强度 | kgf/cm2 | ASTM D-638 | 700 | 80° | |
| 屈服下的伸张强度 | 23° | ASTM D-638 | 1700 | kgf/cm2 | |
| 弯曲弹性率 | 23° | ASTM D-790 | 45000 | kgf/cm2 | |
| 挤剪强度 | 23° | ASTM D-732 | 600 | kgf/cm2 | |
| 弯曲强度 | -30° | ASTM D-790 | 2700 | kgf/cm2 | |
| 抗冲击强度 | 23° | ASTM D-256 | 11 | kgf.cm/cm | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 110 | ||
| 抗冲击强度 | -30° | ASTM D-256 | 8.0 | kgf.cm/cm | |
| 抗冲击强度 | -30° | ASTM D-256 | 14 | kgf.cm/cm | |
| 断裂下的延伸率 | 23° | ASTM D-638 | 6 | % | |
| 屈服下的伸张强度 | 23° | ASTM D-638 | 1000 | kgf/cm2 | |
| 屈服下的伸张强度 | -30° | ASTM D-638 | 2300 | kgf/cm2 | |
| 1%变形下的压缩强度 | 23° | ASTM D-695 | 160 | kgf/cm2 | |
| 弯曲强度 | 80° | ASTM D-790 | 900 | kgf/cm2 | |
| TABER磨耗率 | ASTM D-1044 | 15 | mg | ||
| 屈服下的伸张强度 | kgf/cm2 | ASTM D-638 | 1000 | 80° | |
| 硬度（洛氏、布氏） | 23° | ASTM D-785 | 100 | ||
| 挤剪强度 | 23° | ASTM D-732 | 870 | kgf/cm2 | |
| 弯曲强度 | 23° | ASTM D-790 | 2500 | kgf/cm2 | |
| 屈服下的伸张强度 | -30° | ASTM D-638 | 2000 | kgf/cm2 | |
| 弯曲强度 | -30° | ASTM D-790 | 3000 | kgf/cm2 | |
| 电气性能 | 介电常数 | 103HZ | ASTM D-150 | 4.1 | |
| 体积电阻率 | 4.6kgf/cm2 | ASTM D-257 | 1012 | Ω.cm | |
| 介电损耗 | 103HZ | ASTM D-150 | 0.01 | ||
| 体积电阻率 | ASTM D-257 | 1015 | Ω.cm | ||
| 抗电弧强度 | ASTM D-495 | 121 | S | ||
| 介电损耗 | 60HZ | ASTM D-150 | 0.01 | ||
| 介电常数 | 106HZ | ASTM D-150 | 3.8 | ||
| IEC电路 | UL746 | 500 | V | ||
| 介电常数 | 60HZ | ASTM D-150 | 4.2 | ||
| 介电损耗 | 106HZ | ASTM D-150 | 0.02 | ||
| 热性能 | 热变形温度 | 18.6kgf/cm2 | ASTM D-648 | 215 | °C |
| 熔点 | DSC | 215-225 | °C | ||
| 线性热膨胀系数 | ASTM D-696 | 2.5 | X的10-5cm/cm/°C | ||
| 燃烧率 | UL94 | HB | |||