SABIC HDPE FI0644 产品说明：
SABIC® HDPE FI0644 is a high molecular high density polyethylene copolymer grade specifically desinged for blown film applications. SABIC® HDPE FI0644 features are outstanding toughness and impact properties with very low gel level.
Application
SABIC® HDPE FI0644 is recommended for blown film extrusion. It can be used for producing heavy duty bags, grocery sacks, shopping bags, carier- and T-shirt bags, refuse bags, liners for multi-wall sacks and liners for frozen food meat. The grade is suitable to blend with LLDPE and LDPE and can be used in co-extrusion process.
The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications.
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.944 | g/cm3 | ISO 1183/A |
| 熔流率（熔体流动速率） | ISO 1133 | ||
| 190°C/21.6 kg | 5.4 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 0.18 | g/10 min | ISO 1133 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D) | 60 | ISO 868 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 薄膜厚度 - 经测试 | 20 | μm | |
| 拉伸应力 | ISO 527-3 | ||
| MD : 屈服, 20 μm | 50.0 | MPa | ISO 527-3 |
| TD : 屈服, 20 μm | 45.0 | MPa | ISO 527-3 |
| 伸长率 | ISO 527-3 | ||
| MD : 断裂, 20 μm | 400 | % | ISO 527-3 |
| TD : 断裂, 20 μm | 450 | % | ISO 527-3 |
| 落锤冲击 (20 μm) | 260 | g | ASTM D1709 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 脆化温度 | < -80.0 | °C | ASTM D746 |
| 维卡软化温度 | 73.0 | °C | ISO 306/B |
SABIC HDPE FI0644
基本特性：高密度聚乙烯是一种不透明白色腊状材料，比重比水轻，比重为0.941~0.960，柔软而且有韧性，但比LDPE略硬，也略能伸长，无毒，无味
。
燃烧特性：易燃，离火后能继续燃烧，火焰上端呈黄色，下端呈蓝色，燃烧时会熔融，有液体滴落，无黑烟冒出，同时，发出石蜡燃烧时发出的气味。
主要优点：耐酸碱，耐有机溶剂，电绝缘性优良，低温时，仍能保持一定的韧性。表面硬度，拉伸强度，刚性等机械强度都高于LDPE，接近于PP，比PP韧，但表面光洁度不如PP。
主要缺点：机械性能差，透气差，易变形，易老化，易发脆，脆性低于PP，易应力开裂，表面硬度低，易刮伤。难印刷，印刷时，需进行表面放电处理，不能电镀，表面无光泽。
主要用途：
高密度聚乙烯树脂可采用注射、挤出、吹塑和旋转成型等方法成型塑料制品。采用注射成型可成型出各种类型的容器、工业配件、医用品、玩具、壳体、瓶塞和护罩等制品。采用吹塑成型可成型各种中空容器、超薄型薄膜等。采用挤出成型可成型管材、拉伸条带、捆扎带、单丝、电线和电缆护套等。
另外，还可成型建筑用装饰板、百叶窗、合成木材、合成纸、合成膜和成型钙塑制品等 。