SABIC HDPE PCG4906 产品说明：
SABIC® HDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity.
SABIC® HDPE PCG4906 is typically used for the blow moulding of healthcare industrial packaging (IBC, open head and tight head drums, jerry cans).
The product features good stiffness/ESCR balance combined with good process ability.
Compliance to regulations.
SABIC® HDPE PCG4906 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI).
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.949 | g/cm3 | ISO 1183 |
| 熔流率（熔体流动速率） (190°C/21.6 kg) | 6.0 | g/10 min | ISO 1133 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D, 模压成型) | 60 | ISO 868 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 (2.00 mm, 模压成型) | 950 | MPa | ISO 527-2/1BA/50 |
| 拉伸应力 | ISO 527-2/1BA/50 | ||
| 屈服, 2.00 mm, 模压成型 | 23.0 | MPa | ISO 527-2/1BA/50 |
| 断裂, 2.00 mm, 模压成型 | 34.0 | MPa | ISO 527-2/1BA/50 |
| 拉伸应变 (断裂, 2.00 mm, 模压成型) | > 1000 | % | ISO 527-2/1BA/50 |
| 弯曲模量 (2.00 mm, 模压成型) | 1000 | MPa | ISO 178 |
| 弯曲应力 (2.00 mm, 模压成型) | 24.0 | MPa | ISO 178 |
| ESCR (Strain Hardening) - Gp | 30.0 | MPa | 内部方法 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| Enthalpy Change | 192 | J/g | ISO 11357-3 |
管材特性
HDPE是一种好的管道，不仅应具有良好的经济性，而且应具备接口稳定可靠、材料抗冲击、抗开裂、耐老化、耐腐蚀等一系列优点，同传统管材相比，HDPE管道系统具有以下一系列优点：
⑴连接可靠：聚乙烯管道系统之间采用电热熔方式连接，接头的强度高于管道本体强度。
⑵低温抗冲击性好：聚乙烯的低温脆化温度极低，可在-60-60℃温度范围内安全使用。冬季施工时，因材料抗冲击性好，不会发生管子脆裂。
⑶抗应力开裂性好：HDPE具有低的缺口敏感性、高的剪切强度和优异的抗刮痕能力，耐环境应力开裂性能也非常突出。
⑷耐化学腐蚀性好：HDPE管道可耐多种化学介质的腐蚀，土壤中存在的化学物质不会对管道造成任何降解作用。聚乙烯是电的绝缘体，因此不会发生腐烂、生锈或电化学腐蚀现象;此外它也不会促进藻类、细菌或真菌生长。
⑸耐老化，使用寿命长：含有2-2.5%的均匀分布的碳黑的聚乙烯管道能够在室外露天存放或使用50年，不会因遭受紫外线辐射而损害。
⑹耐磨性好：HDPE管道与钢管的耐磨性对比试验表明，HDPE管道的耐磨性为钢管的4倍。在泥浆输送领域，同钢管相比，HDPE管道具有更好的耐磨性，这意味着HDPE管道具有更长的使用寿命和更好的经济性。