SABIC HDPE PCG453 产品说明：
SABIC® HDPE M453SE is typically used for the high demanding dustbin market. It is an UV stabilized HDPE copolymer grade. It typically shows a good combination of processability, consistency and product properties, good stiffness/cold impact-balance, surface quality and weatherability properties.
Typical applications.
SABIC® HDPE M453SE is typically used for the manufacture of injection molded dustbins (waste containers on wheels and household containers), crates & boxes (pallet boxes, pallets, boxes applied at low temperatures) and pails & container applications (industrial, shipping).
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.953 | g/cm3 | ISO 1183 |
| 熔流率（熔体流动速率） | ISO 1133 | ||
| 190°C/2.16 kg | 4.0 | g/10 min | ISO 1133 |
| 190°C/5.0 kg | 11 | g/10 min | ISO 1133 |
| 抗环境应力开裂 1(60°C, 3.00 mm, Rhodacal-DS10, 模压成型) | 65.0 | hr | 内部方法 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D, 模压成型) | 61 | ISO 868 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 拉伸模量 (2.00 mm, 模压成型) | 1100 | MPa | ISO 527-2/1BA/50 |
| 拉伸应力 | ISO 527-2/1BA/50 | ||
| 屈服, 2.00 mm, 模压成型 | 26.0 | MPa | ISO 527-2/1BA/50 |
| 断裂, 2.00 mm, 模压成型 | 31.0 | MPa | ISO 527-2/1BA/50 |
| 拉伸应变 (断裂, 2.00 mm, 模压成型) | > 200 | % | ISO 527-2/1BA/50 |
| 弯曲模量 (2.00 mm, 模压成型) | 1200 | MPa | ISO 178 |
| 弯曲应力 (2.00 mm, 模压成型) | 26.0 | MPa | ISO 178 |
SABIC HDPE PCG453
基本特性：高密度聚乙烯是一种不透明白色腊状材料，比重比水轻，比重为0.941~0.960，柔软而且有韧性，但比LDPE略硬，也略能伸长，无毒，无味
。
燃烧特性：易燃，离火后能继续燃烧，火焰上端呈黄色，下端呈蓝色，燃烧时会熔融，有液体滴落，无黑烟冒出，同时，发出石蜡燃烧时发出的气味。
主要优点：耐酸碱，耐有机溶剂，电绝缘性优良，低温时，仍能保持一定的韧性。表面硬度，拉伸强度，刚性等机械强度都高于LDPE，接近于PP，比PP韧，但表面光洁度不如PP。
主要缺点：机械性能差，透气差，易变形，易老化，易发脆，脆性低于PP，易应力开裂，表面硬度低，易刮伤。难印刷，印刷时，需进行表面放电处理，不能电镀，表面无光泽。
主要用途：
高密度聚乙烯树脂可采用注射、挤出、吹塑和旋转成型等方法成型塑料制品。采用注射成型可成型出各种类型的容器、工业配件、医用品、玩具、壳体、瓶塞和护罩等制品。采用吹塑成型可成型各种中空容器、超薄型薄膜等。采用挤出成型可成型管材、拉伸条带、捆扎带、单丝、电线和电缆护套等。
另外，还可成型建筑用装饰板、百叶窗、合成木材、合成纸、合成膜和成型钙塑制品等 。