SABIC HDPE PCG453 产品说明：

SABIC® HDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity.

SABIC® HDPE PCG453 is typically used for the injection moulding of healthcare packaging, caps and closures and other parts for medical packaging. This grade has a very high impact resistance, even at low temperatures.

Compliance to regulations.
SABIC® HDPE PCG453 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI).

物理性能	额定值	单位制	测试方法
密度	0.953	g/cm3	ISO 1183
熔流率（熔体流动速率）			ISO 1133
190°C/2.16 kg	4.7	g/10 min	ISO 1133
190°C/5.0 kg	13	g/10 min	ISO 1133
抗环境应力开裂 1(60°C, 3.00 mm, Rhodacal-DS10, 模压成型)	95.0	hr	内部方法

硬度	额定值	单位制	测试方法
肖氏硬度 (邵氏 D, 模压成型)	61		ISO 868

机械性能	额定值	单位制	测试方法
拉伸模量 (2.00 mm, 模压成型)	1100	MPa	ISO 527-2/1BA/50
拉伸应力			ISO 527-2/1BA/50
屈服, 2.00 mm, 模压成型	26.0	MPa	ISO 527-2/1BA/50
断裂, 2.00 mm, 模压成型	25.0	MPa	ISO 527-2/1BA/50
拉伸应变 (断裂, 2.00 mm, 模压成型)	> 200	%	ISO 527-2/1BA/50
弯曲模量 (2.00 mm, 模压成型)	1200	MPa	ISO 178
弯曲应力 (2.00 mm, 模压成型)	26.0	MPa	ISO 178

HDPE特性：

高密度聚乙烯具有良好的耐热性和耐寒性，化学稳定性好，还具有较高的刚性和韧性，机械强度好。介电性能，耐环境应力开裂性亦较好。硬度、拉伸强度和蠕变性优于低密度聚乙烯；耐磨性、电绝缘性、韧性及耐寒性均较好，但与低密度绝缘性比较略差些；化学稳定性好，在室温条件下，不溶于任何有机溶剂，耐酸、碱和各种盐类的腐蚀；薄膜对水蒸气和空气的渗透性小、吸水性低；耐老化性能差，耐环境开裂性不如低密度聚乙烯，特别是热氧化作用会使其性能下降，所以，树脂需加入抗氧剂和紫外线吸收剂等来提高改善这方面的不足。高密度聚乙烯薄膜在受力情况下的热变形温度较低，这一点应用时要注意。

应用：用于挤出包装薄膜，绳索，编织袋，渔网，水管；注塑低档日用品及外壳，非承载荷构件，胶箱，周转箱；挤出吹塑容器，中空制品，瓶子。

SABIC HDPE PCG453 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！ 

我司供应其它品牌原料:

通用型塑胶原料种类如下：

ABS ABS高胶粉 ADPOLY AS(SAN) CA CAB EAA EVA GPPS HDPE HIPS LDPE LLDPE MBS MDPE MS MVLDPE(茂金属) PP PVC ULDPE

工程塑胶原料种类如下：

PA （尼龙）类 ： 包括PA6 PA66 PA12 PA11 PA612 PA610 PA46 

高耐温材料 ：LCP PEEK PEI PPA PTFE PVDF 

合金类： PA+ABS PC+ABS PA+PTFE POM+PTFE PC/TPFE PBT/ABS PBT/ASA PBT/F/PTFE PBT/PC PBT/PET 

高刚性材料类： POM 以有 POM加各种填充合金

 热塑弹性体： BR EMA CPE OBCs POE PBE POP SBR SBS SEBS SURLYN SIS SSBR TPE TPEE TPO TPR TPSIV TPU TPV TPX