东莞市塑宇化工有限公司
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | 24hr | ASTM D-570 | ||
| DAM｜50%RH | |||||
| 0.5｜- | |||||
| % | ||||
| 物理性能 | 比重 | ASTM D-792 | ||
| DAM｜50%RH | ||||
| 1.56｜- |
| 模具收缩率 | 3.2mm,flow | ASTM D-792 | |
| DAM｜50%RH | |||
| 0.4｜- |
| % | ||||
| 机械性能 | 弯曲强度 | ASTM D-790 | ||
| DAM｜50%RH | ||||
| 240｜- | ||||
| MPa | |||
| 断裂伸长率 | ASTM D-638 | ||
| DAM｜50%RH | |||
| 2.5｜4 |
| % | |||
| IZOD缺口冲击强度 | ASTM D-256 | ||
| DAM｜50%RH | |||
| 100｜105 |
| J/m | |||
| 弯曲模量 | ASTM D-790 | ||
| DAM｜50%RH | |||
| 8960｜6900 |
| MPa | |||
| 拉伸强度 | ASTM D-638 | ||
| DAM｜50%RH | |||
| 169｜134 |
| MPa | ||||
| 电气性能 | 体积电阻率 | ASTM D-257 | ||
| DAM｜50%RH | ||||
| 1014｜1011 | ||||
| Ω.cm | |||
| 损耗因数 | 103Hz | ASTM D-150 | |
| DAM｜50%RH | DAM｜50%RH | ||
| 0.｜541 | 0.009｜0.113 |
| 介电常数 | 103Hz | ASTM D-150 | |
| DAM｜50%RH | |||
| 3.6｜5.1 |
| 表面电阻率 | ASTM D-257 | ||
| DAM｜50%RH | |||
| 1014｜1011 |
| Ω | |||
| 介电强度 | 3.2mm | ASTM D-149 | |
| DAM｜50%RH | |||
| 17.2｜15.6 |
| kv/mm | |||
| 损耗因数 | 106Hz | ASTM D-150 | |
| DAM｜50%RH | |||
| 0.014｜0.041 |
| 介电常数 | 106Hz | ASTM D-150 | |
| DAM｜50%RH | |||
| 3.5｜3.8 |
| 热性能 | 热变形温度 | 0.45MPa | ASMT D-648 | |
| DAM｜50%RH | ||||
| 257｜- |
| ℃ | |||
| 热变形温度 | 1.80MPa | ASTM D-648 | |
| DAM｜50%RH | |||
| 235｜- |
| MPa | |||
| 熔点 | ASTM D-3418 | ||
| DAM｜50%RH | |||
| 262｜- |
| ℃ |