东莞市塑宇化工有限公司
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D-792 | 1.62 | ||
| 模具收缩率 | 1.6mm(0.063in) | ASTM D-955 | -0.1 | % | |
| 机械性能 | 弯曲模量 | 1.6mm(0.063in),23℃(73℉) | ASTM D-790 | 14000 | MPa |
| IZOD冲击强度 | 3.2mm(0.125in),23℃(73℉) | ASTM D-256 | 225 | J/m | |
| 拉伸强度 | 1.6mm(0.063in),23℃(73℉) | ASTM D-638 | 173 | MPa | |
| 拉伸模量 | 1.6mm(0.063in),23℃(73℉) | ASTM D-638 | 19306 | MPa | |
| IZOD冲击强度 | 1.6mm(0.063in),23℃(73℉) | ASTM D-256 | 170 | J/m | |
| 拉伸强度 | 3.2mm(0.125in),23℃(73℉) | ASTM D-638 | 150 | MPa | |
| 弯曲强度 | 0.8mm(0.032in),23℃(73℉) | ASTM D-790 | 215 | MPa | |
| 无缺口冲击强度 | 3.2mm(0.125in),23℃(73℉) | ASTM D-4812 | 740，20%NB | J/m | |
| 弯曲模量 | 0.8mm(0.032in),23℃(73℉) | ASTM D-790 | 18000 | MPa | |
| 弯曲强度 | 3.2mm(0.125in),23℃(73℉) | ASTM D-790 | 183 | MPa | |
| 压缩强度 | 3.2mm(0.125in) | ASTM D-695 | 89 | MPa | |
| 断裂伸长率 | 1.6mm(0.063in),23℃(73℉) | ASTM D-638 | 1.6 | % | |
| 弯曲模量 | 3.2mm(0.125in),23℃(73℉) | ASTM D-790 | 13100 | MPa | |
| IZOD冲击强度 | 0.8mm(0.032in),23℃(73℉) | ASTM D-256 | 400,40%NB | J/m | |
| 剪切强度 | 0.8mm(0.032in) | ASTM D-732 | 57 | MPa | |
| 弯曲强度 | 1.6mm(0.063in),23℃(73℉) | ASTM D-790 | 192 | MPa | |
| 断裂伸长率 | 3.2mm(0.125in) | ASTM D-638 | 1.7 | % | |
| 无缺口冲击强度 | 1.6mm(0.063in),23℃(73℉) | ASTM D-4812 | 840 | J/m | |
| 洛氏硬度 | ASTM D-785 | 63 | |||
| 拉伸模量 | 3.2mm(0.125in),23℃(73℉) | ASTM D-638 | 18000 | MPa | |
| 压缩模量 | 3.2mm(0.125in) | ASTM D-695 | 5300 | MPa | |
| 剪切强度 | 3.2mm(0.125in) | ASTM D-732 | 58 | MPa | |
| 无缺口冲击强度 | 0.8mm(0.032in),23℃(73℉) | ASTM D-4812 | NB | J/m | |
| 电气性能 | 损耗因数 | 3.2mm(0.125in),23℃(73℉) | ASTM D-2520 B | 0.004 | |
| 介电常数 | 3.2mm(0.125in),23℃(73℉) | ASTM D-2520 B | 4.3 | ||
| 损耗因数 | 3.2mm(0.125in),23℃(73℉) | ASTM D-150 | 0.029 | ||
| 介电常数 | 3.2mm(0.125in),23℃(73℉) | ASTM D-150 | 3.8 | ||
| 介电常数 | 0.8mm(0.032in),23℃(73℉) | ASTM D-150 | 3.5 | ||
| 介电常数 | 0.8mm(0.032in),23℃(73℉) | ASTM D-2520 B | 4.4 | ||
| 损耗因数 | 3.2mm(0.125in),23℃(73℉) | ASTM D-150 | 0.013 | ||
| 损耗因数 | 0.8mm(0.032in),23℃(73℉) | ASTM D-150 | 0.029 | ||
| 介电常数 | 1.6mm(0.063in),23℃(73℉) | ASTM D-2520 B | 4.3 | ||
| 表面电阻率 | ASTM D-257 | 1×1015 | Ohm | ||
| 介电常数 | 0.8mm(0.032in),23℃(73℉) | ASTM D-150 | 3.9 | ||
| 介电常数 | 3.2mm(0.125in),23℃(73℉) | ASTM D-150 | 4.3 | ||
| 体积电阻率 | ASTM D-257 | 1×1016 | Ohm-cm | ||
| 介电强度 | 3.2mm,23℃(73℉) | ASTM D-149 | >28 | Kv/mm | |
| 损耗因数 | 1.6mm(0.063in),23℃(73℉) | ASTM D-2520 B | 0.004 | ||
| 介电强度 | 1.6mm,23℃(73℉) | ASTM D-149 | 35 | Kv/mm | |
| 损耗因数 | 0.8mm(0.032in),23℃(73℉) | ASTM D-150 | 0.013 | ||
| 损耗因数 | 0.8mm(0.032in),23℃(73℉) | ASTM D-2520 B | 0.004 | ||
| 介电强度 | 1.6mm(0.063in) | ASTM D-149 | 31 | Kv/mm | |
| 热性能 | 表面电阻率 | ASTM D-257 | 1×1015 | Ohm | |
| 熔点 | ASTM D-3418 | 352 | ℃ | ||
| 解链温度范围 | 363-371 | ℃ | |||
| 热导率 | ASTM C-177 | 0.32 | W/mk | ||
| 模压温度范围 | 30-95 | ℃ | |||
| 玻璃化转变温度 | ASTM D-3418 | 120 | ℃ | ||
| 干燥温度 | 135 | ℃ | |||
| 热变形温度 | 1.80MPa | ASTM D-648 | 289 | ℃ | |
| 其它性能 | RTI,Mechanical with Impact | 1.5mm | UL 746-B | 210 | ℃ |
| RTI,Electrical | 3.0mm | UL 746-B | 240 | ℃ | |
| RTI,Mechanical without Impact | 1.5mm | UL 746-B | 240 | ℃ | |
| RTI,Electrical | 0.75mm | UL 746-B | 240 | ℃ | |
| RTI,Mechanical without Impact | 0.75mm | UL 746-B | 240 | ℃ | |
| RTI,Mechanical with Impact | 3.0mm | UL 746-B | 210 | ℃ | |
| RTI,Mechanical without Impact | 3.0mm | UL 746-B | 240 | ℃ | |
| RTI,Electrical | 1.5mm | UL 746-B | 240 | ℃ | |