COC TOPAS 6013M-07 产品说明：

Product Description
TOPAS 6013M-07 is an injection molding grade with a wide processing window, especially suited for blow molding processes including IBM and ISBM. It is a glass-clear amorphous polymer with outstanding moisture barrier, chemical resistance, high purity and a non-reactive surface making it an excellent choice for healthcare and other high-tech products. Lower leachables and extractables of TOPAS COC preserve content stability and quality. It is a non-polar substrate that does not promote adsorption, denaturation, aggregation, or precipitation like glass can. This grade has a high (130°C) heat distortion temperature to withstand 121°C steam sterilization protocols, as well as gamma and EtO procedures.

物理性能	额定值	单位制	测试方法
密度	1.02	g/cm3	ISO 1183
熔流率（熔体流动速率） (260°C/2.16 kg)	12	g/10 min	ISO 1133
溶化体积流率（MVR） (260°C/2.16 kg)	13.0	cm3/10min	ISO 1133
收缩率 1	0.50 到 0.70	%	内部方法
吸水率 (饱和, 23°C)	0.010	%	ISO 62

机械性能	额定值	单位制	测试方法
拉伸模量	2900	MPa	ISO 527-2/1A/1
拉伸应力 (屈服)	63.0	MPa	ISO 527-2/1A/50
拉伸应变 (屈服)	2.6	%	ISO 527-2/1A/50

冲击性能	额定值	单位制	测试方法
简支梁缺口冲击强度 (23°C)	2.0	kJ/m2	ISO 179/1eA
简支梁无缺口冲击强度 (23°C)	14	kJ/m2	ISO 179/1eU

热性能	额定值	单位制	测试方法
热变形温度 (0.45 MPa, 未退火)	130	°C	ISO 75-2/B
玻璃转化温度	142	°C	ISO 11357-2

COC特性：

环烯烃共聚物 是一种无定形高分子聚合物制造商生产的几个。 COC是一类新的聚合物相对较 聚丙烯 和 聚乙烯。这种材料主要用于要求玻璃般清晰包括镜头，瓶，显示器和医疗

设备的应用程序。COCs良好的耐化学性。

挤压 COC既可以挤压铸造和吹膜设备。主要用于消费应用，包括食品和药品包装。

成型 COC是主要用于注射成型。

TOPAS是宝理公司开发出来的环烯烃类共聚物（COC）的商品名，是具有环状烯烃结构的非晶性透明共聚高分子。

TOPAS 具有与PMMA（聚甲基丙烯酸甲酯、丙烯酸树脂）相匹敌的光学性能以及具有高于PC（聚碳酸酯）的耐热性，还具有比PMMA和PC更加优良的尺寸稳定性等，在市场上获得了很

高的评价。再有，TOPAS 还具有改善水蒸汽气密性，增加刚性、耐热性，易赋予切割性能等优点，作为适合于用作传统材料的改性用材料，它在包装材料领域里的开发活动正在推进之中。是玻璃材料的最佳替代材料。

COC TOPAS 6013M-07 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！