SABIC HDPE PCG5421 产品说明：

SABIC® HDPE grades for healthcare applications are produced under controlled conditions resulting in high product quality, consistency and a high level of purity.

SABIC® HDPE PCG5421 is typically used for the blow moulding of healthcare packaging (bottles and cans). The product features a good stiffness/ESCR balance combined with good process ability.

Compliance to regulations
SABIC® HDPE PCG5421 complies with the relevant monographs of the European Pharmacopoeia (EP) and the United States Pharmacopoeia (USPVI).

物理性能	额定值	单位制	测试方法
密度	0.954	g/cm3	ISO 1183
熔流率（熔体流动速率）			ISO 1133
190°C/2.16 kg	0.16	g/10 min	ISO 1133
190°C/21.6 kg	20	g/10 min	ISO 1133
190°C/5.0 kg	0.89	g/10 min	ISO 1133
抗环境应力开裂 1(75°C, 1.00 mm, Rhodacal-DS10, 模压成型)	16.0	hr	内部方法

硬度	额定值	单位制	测试方法
肖氏硬度 (邵氏 D, 模压成型)	61		ISO 868

机械性能	额定值	单位制	测试方法
拉伸模量 (2.00 mm, 模压成型)	1050	MPa	ISO 527-2/1BA/50
拉伸应力			ISO 527-2/1BA/50
屈服, 2.00 mm, 模压成型	26.0	MPa	ISO 527-2/1BA/50
断裂, 2.00 mm, 模压成型	27.0	MPa	ISO 527-2/1BA/50
拉伸应变 (断裂, 2.00 mm, 模压成型)	> 1000	%	ISO 527-2/1BA/50
弯曲模量 (2.00 mm, 模压成型)	1250	MPa	ISO 178
弯曲应力 (2.00 mm, 模压成型)	27.0	MPa	ISO 178

管材特性

HDPE是一种好的管道，不仅应具有良好的经济性，而且应具备接口稳定可靠、材料抗冲击、抗开裂、耐老化、耐腐蚀等一系列优点，同传统管材相比，HDPE管道系统具有以下一系列优点：

⑴连接可靠：聚乙烯管道系统之间采用电热熔方式连接，接头的强度高于管道本体强度。

⑵低温抗冲击性好：聚乙烯的低温脆化温度极低，可在-60-60℃温度范围内安全使用。冬季施工时，因材料抗冲击性好，不会发生管子脆裂。

⑶抗应力开裂性好：HDPE具有低的缺口敏感性、高的剪切强度和优异的抗刮痕能力，耐环境应力开裂性能也非常突出。

⑷耐化学腐蚀性好：HDPE管道可耐多种化学介质的腐蚀，土壤中存在的化学物质不会对管道造成任何降解作用。聚乙烯是电的绝缘体，因此不会发生腐烂、生锈或电化学腐蚀现象;此外它也不会促进藻类、细菌或真菌生长。

⑸耐老化，使用寿命长：含有2-2.5%的均匀分布的碳黑的聚乙烯管道能够在室外露天存放或使用50年，不会因遭受紫外线辐射而损害。

⑹耐磨性好：HDPE管道与钢管的耐磨性对比试验表明，HDPE管道的耐磨性为钢管的4倍。在泥浆输送领域，同钢管相比，HDPE管道具有更好的耐磨性，这意味着HDPE管道具有更长的使用寿命和更好的经济性。

SABIC HDPE PCG5421 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料，价格最优，质量保证！