HDPE特性:
高密度聚乙烯具有良好的耐热性和耐寒性,化学稳定性好,还具有较高的刚性和韧性,机械强度好。介电性能,耐环境应力开裂性亦较好。硬度、拉伸强度和蠕变性优于低密度聚乙烯;耐磨性、电绝缘性、韧性及耐寒性均较好,但与低密度绝缘性比较略差些;化学稳定性好,在室温条件下,不溶于任何有机溶剂,耐酸、碱和各种盐类的腐蚀;薄膜对水蒸气和空气的渗透性小、吸水性低;耐老化性能差,耐环境开裂性不如低密度聚乙烯,特别是热氧化作用会使其性能下降,所以,树脂需加入抗氧剂和紫外线吸收剂等来提高改善这方面的不足。高密度聚乙烯薄膜在受力情况下的热变形温度较低,这一点应用时要注意。
应用:用于挤出包装薄膜,绳索,编织袋,渔网,水管;注塑低档日用品及外壳,非承载荷构件,胶箱,周转箱;挤出吹塑容器,中空制品,瓶子。
SABIC HDPE M80064 产品说明:
SABIC® HDPE M80064 is a high density polyethylene injection moulding grade with a narrow molecular weight distribution. It is typically used for injection moulding applications where rigidity, toughness and warp resistance are required. SABIC® HDPE M80064 is available with UV stabilizer as SABIC® HDPE M80064S.
Typical applications.
SABIC® HDPE M80064 is typically used for the manufacture of injection moulded cases, crates, trays, industrial pails and other similar items.
This product is not intended for and must not be used in any pharmaceutical/medical applications.
物理性能 |
额定值 |
单位制 |
测试方法 |
密度 |
0.964 |
g/cm3 |
ISO 1183 |
熔流率(熔体流动速率) |
|
|
ISO 1133 |
190°C/2.16 kg |
8.0 |
g/10 min |
ISO 1133 |
190°C/5.0 kg |
22 |
g/10 min |
ISO 1133 |
抗环境应力开裂 1(60°C, 3.00 mm, Rhodacal-DS10, 模压成型) |
40.0 |
hr |
内部方法 |
硬度 |
额定值 |
单位制 |
测试方法 |
肖氏硬度 (邵氏 D, 模压成型) |
65 |
|
ISO 868 |
机械性能 |
额定值 |
单位制 |
测试方法 |
拉伸模量 (2.00 mm, 模压成型) |
1450 |
MPa |
ISO 527-2/1BA/50 |
拉伸应力 |
|
|
ISO 527-2/1BA/50 |
屈服, 2.00 mm, 模压成型 |
32.0 |
MPa |
ISO 527-2/1BA/50 |
断裂, 2.00 mm, 模压成型 |
15.0 |
MPa |
ISO 527-2/1BA/50 |
拉伸应变 (断裂, 2.00 mm, 模压成型) |
> 200 |
% |
ISO 527-2/1BA/50 |
弯曲模量 (2.00 mm, 模压成型) |
1700 |
MPa |
ISO 178 |
弯曲应力 (2.00 mm, 模压成型) |
32.0 |
MPa |
ISO 178 |
冲击性能 |
额定值 |
单位制 |
测试方法 |
悬壁梁缺口冲击强度 (23°C, 模压成型) |
4.0 |
kJ/m2 |
ISO 180/A |
热性能 |
额定值 |
单位制 |
测试方法 |
热变形温度 (0.45 MPa, 未退火) |
95.0 |
°C |
ISO 75-2/B |
维卡软化温度 |
129 |
°C |
ISO 306/A |
溶融温度(DSC) |
135 |
°C |
ISO 11357-3 |
Enthalpy Change |
229 |
J/g |
ISO 11357-3 |
SABIC HDPE M80064 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料,价格最优,质量保证!