COC TOPAS 5013L-10 产品说明:
Product Description
TOPAS 5013L-10 is a high flow, internally lubricated injection molding grade with a 130°C heat distortion temperature. It is a glass-clear amorphous polymer with outstanding moisture barrier, chemical resistance, high purity and a non-reactive surface making it an excellent choice for healthcare and other high-tech products. The 5013 resin series features high flow characteristics for excellent mold detail replication. This grade has a high heat distortion temperature to withstand 95°C PCR protocols, is suitable for gamma or EtO procedures.
物理性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
密度 | 1.02 | g/cm3 | ISO 1183 |
熔流率(熔体流动速率) (260°C/2.16 kg) | 44 | g/10 min | ISO 1133 |
溶化体积流率(MVR) (260°C/2.16 kg) | 48.0 | cm3/10min | ISO 1133 |
收缩率 1 | 0.10 到 0.30 | % | 内部方法 |
吸水率 (饱和, 23°C) | 0.010 | % | ISO 62 |
机械性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
拉伸模量 | 3200 | MPa | ISO 527-2/1A/1 |
拉伸应力 (屈服) | 46.0 | MPa | ISO 527-2/1A/50 |
拉伸应变 (屈服) | 1.7 | % | ISO 527-2/1A/50 |
冲击性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
简支梁缺口冲击强度 (23°C) | 1.6 | kJ/m2 | ISO 179/1eA |
简支梁无缺口冲击强度 (23°C) | 13 | kJ/m2 | ISO 179/1eU |
热性能 | 额定值 | 单位制 | 测试方法 |
---|---|---|---|
热变形温度 (0.45 MPa, 未退火) | 127 | °C | ISO 75-2/B |
玻璃转化温度 | 134 | °C | ISO 11357-2 |
药物输送精密,部件预充式注射器,西林瓶,子弹瓶和管手术器械四,容器和组件您高温光学电子食品包装医疗保健和食品接触
领导属性
低溶出物和萃取物,低水传输尺寸稳定性,高公差非离子型,不提倡像玻璃吸附微反应醇,丙酮,和丙烯酸酯的化学耐受性透明,可承受ETO /伽玛/蒸汽灭菌耐温性,清晰度和纯度净度,低双折射,潮湿敏感度低;低介电常数,热塑性不制造双酚A,邻苯二甲酸盐或卤素广泛的合规性
相关牌号为注塑,医疗,光学和诊断
TOPAS 6013M-07 - 更广泛的加工窗口,最好的吹塑(IBM / ISBM)TOPAS 6015S-04 - 高耐热变形性(150℃)为134°C的协议TOPAS IT的应用需要额外的韧性X1 - 冲级。
COC TOPAS 5013L-10 可提供COA、COC,ROHS.MSDS.UL黄卡等等资料,价格最优,质量保证!
COC TOPAS 5013L-10
COC TOPAS 6015S-04
COC TOPAS 8007F-600
COC TOPAS 8007S-04
COC TOPAS 8007F-400
COC TOPAS 8007F-04
COC TOPAS 6017S-04
COC TOPAS 8007D-61
COC TOPAS 7010F-600
COC TOPAS 9903D-10
COC TOPAS 6017S-04
COC TOPAS 8007F-04
COC TOPAS 8007S-04