高性能树脂的优势：

1. 采用更轻的解决方案，可降低燃油消耗并减少对环境的影响

2. 在很宽的温度范围内保持优异的弹性性能，从而延长零件使用寿命

3. 优异的耐磨性，增加部件的耐用性

4. 耐腐蚀性化学品和天然元素，从而减少停机时间和部件失效

5. 值得信赖的长期力学性能和尺寸稳定性

6. 符合严格的安全要求，具有阻燃、低烟和低毒排放等特点

7. 对各种液体和油脂具有优异的阻隔性，从而保证更高的零件综合性能
   

TYPICAL PROPERTIES (1)
MECHANICAL	Value	Unit	Standard
Tensile Stress, break	2300	kgf/cm2	ASTM D 638
Tensile Strain, break	1.5	%	ASTM D 638
Tensile Modulus, 50 mm/min	313500	kgf/cm2	ASTM D 638
Flexural Stress	3310	kgf/cm2	ASTM D 790
Flexural Modulus	205900	kgf/cm2	ASTM D 790
Tensile Stress, break	230	MPa	ISO 527
Tensile Strain, break	1.5	%	ISO 527
Tensile Modulus, 1 mm/min	24700	MPa	ISO 527
Flexural Stress	346	MPa	ISO 178
Flexural Modulus	24300	MPa	ISO 178
IMPACT	Value	Unit	Standard
Izod Impact, unnotched, 23°C	62	cm-kgf/cm	ASTM D 4812
Izod Impact, notched, 23°C	7	cm-kgf/cm	ASTM D 256
Instrumented Impact Energy @ peak, 23°C	127	cm-kgf	ASTM D 3763
Izod Impact, unnotched 80*10*4  23°C	42	kJ/m2	ISO 180/1U
Izod Impact, notched 80*10*4  23°C	7	kJ/m2	ISO 180/1A
THERMAL	Value	Unit	Standard
HDT, 0.45 MPa, 3.2 mm, unannealed	>298	°C	ASTM D 648
HDT, 1.82 MPa, 3.2mm, unannealed	>298	°C	ASTM D 648
CTE, -40°C to 40°C, flow	1.2E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, xflow	2.93E-05	1/°C	ASTM E 831
CTE, -40°C to 40°C, flow	1.21E-05	1/°C	ISO 11359-2
CTE, -40°C to 40°C, xflow	2.93E-05	1/°C	ISO 11359-2
HDT/Bf, 0.45 MPa Flatw 80*10*4 sp=64mm	>240	°C	ISO 75/Bf
HDT/Af, 1.8 MPa Flatw 80*10*4 sp=64mm	>240	°C	ISO 75/Af
PHYSICAL	Value	Unit	Standard
Density	1.413	g/cm3	ASTM D 792
Moisture Absorption, 50% RH, 24 hrs	0.08	%	ASTM D 570
Mold Shrinkage, flow, 24 hrs (5)	0.1	%	ASTM D 955
Mold Shrinkage, xflow, 24 hrs (5)	0.4	%	ASTM D 955
Mold Shrinkage, flow, 24 hrs (5)	0.12	%	ISO 294
Mold Shrinkage, xflow, 24 hrs (5)	0.4	%	ISO 294
Wear Factor Washer	55	10^-10 in^5-min/ft-lb-hr	ASTM D 3702 Modified: Manual
Dynamic COF	0.3	-	ASTM D 3702 Modified: Manual
Static COF	0.32	-	ASTM D 3702 Modified: Manual
Density	1.4	g/cm3	ISO 1183
Moisture Absorption (23°C / 50% RH)	0.07	%	ISO 62
FLAME CHARACTERISTICS	Value	Unit	Standard
UL Compliant, 94V-0 Flame Class Rating (3)(4)	0.77	mm	UL 94 by SABIC-IP

Parameter
Injection Molding	Value	Unit
Drying Temperature	150	°C
Drying Time	4 - 6	hrs
Front - Zone 3 Temperature	380 - 400	°C
Middle - Zone 2 Temperature	380 - 400	°C
Rear - Zone 1 Temperature	370 - 380	°C
Mold Temperature	175 - 190	°C
Back Pressure	0.3 - 0.7	MPa
Screw Speed	60 - 100	rpm

   为航空业带来的效益：

• 与同类不锈钢管道相比，减重高达60%

• 可弯曲和成型，适用于设计复杂管道系统

• 经航空航天行业主要飞机OEM厂商认证，拥有25年良好业绩

• 无腐蚀性并且对航空航天液体具有优异的耐受性

• 具有光滑内表面，使用时可减少液体摩擦损失

• 具有减振性

• 具有很高的延展性和坚韧性，可耐受很高的变形度而不会断裂

• 为能源行业带来的效益：  

• 与昂贵的耐腐性合金相比具有成本效益

• 重量轻并且安装灵活和易于缠绕

• 高机械强度并且在极端温度条件下具有高延展性

• 对油田化学品具有高度耐受性，可延长使用寿命，210°C (410°F)条件下的酸气老化性能超过NORSOK M710的要求

• 在严酷环境中可耐受应力腐蚀裂纹和斑蚀

• 优异的快速气体减压（RGD）性能