东莞市塑宇化工有限公司
塑宇销售PCABS基础创新塑料C6200-701.塑胶原料
SABIC Innovative Plastics Cycoloy® C6200 PC+ABS
Polymer,Thermoplastic,ABS Polymer,Polycarbonate/ABS Alloy, Unreinforced,Polycarbonate (PC)
SABIC Innovative Plastics (GE Plastics)
产品说明:
Non-chlorinated, nombrominated flame retardant PC/ABS offering balanced heat, flow and impact to meet various application needs.
C6200-701 PC+ABS 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| 线性成型收缩率,Flow | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| 线性成型收缩率，横向 | 0.0040 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0060 in/in @Thickness 0.126 in |
SABIC Method |
| 熔体流动速率 | 14.5 g/10 min @Load 2.16 kg, Temperature 260 °C |
14.5 g/10 min @Load 4.76 lb, Temperature 500 °F |
ASTM D1238 |
| Spiral Flow | 68.58 cm @Temperature 260 °C |
27.00 in @Temperature 500 °F |
10 ips,3.175 X 1524 mm |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(屈服) | 66.0 MPa | 9570 psi | Type I, 50 mm/min; ASTM D638 |
| 伸长率 (断裂) | 50 % | 50 % | Type I, 50 mm/min; ASTM D638 |
| 弯曲强度 | 103 MPa | 14900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 弯曲模量 | 2.68 GPa | 389 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 悬壁梁缺口冲击强度 | 5.34 J/cm | 10.0 ft-lb/in | ASTM D256 |
| 落锤总能量 | 61.0 J | 45.0 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| 54.0 J @Temperature -30.0 °C |
39.8 ft-lb @Temperature -22.0 °F |
Instrumented Impact Energy @ peak; ASTM D3763 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | IEC 60093 |
| 表面电阻 | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| 介电常数 | 2.7 @Frequency 1.00e+6 Hz |
2.7 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 2.8 @Frequency 50.0 - 60.0 Hz |
2.8 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| 介电强度 | 17.0 kV/mm @Thickness 3.20 mm |
432 kV/in @Thickness 0.126 in |
in oil; IEC 60243-1 |
| 25.0 kV/mm @Thickness 1.60 mm |
635 kV/in @Thickness 0.0630 in |
in oil; IEC 60243-1 | |
| 35.0 kV/mm @Thickness 0.800 mm |
889 kV/in @Thickness 0.0315 in |
in oil; IEC 60243-1 | |
| 耗散因数 | 0.0040 @Frequency 50.0 - 60.0 Hz |
0.0040 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.0080 @Frequency 1.00e+6 Hz |
0.0080 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| 耐电弧性 | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| 相比耐漏电起痕指数(CTI) | 250 - 400 V | 250 - 400 V | UL 746A |
| 热丝引燃 (HWI) | 30 - 60 sec | 30 - 60 sec | UL 746A |
| 高电弧燃烧，HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| 高压电弧跟踪率，HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | UL 746A |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 87.0 °C @Thickness 3.20 mm |
189 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| 90.0 °C @Thickness 6.40 mm |
194 °F @Thickness 0.252 in |
unannealed; ASTM D648 | |
| UL RTI | 85.0 °C | 185 °F | UL 746B |
| UL RTI，机械冲击 | 85.0 °C | 185 °F | UL 746B |
| UL RTI，机械无冲击 | 85.0 °C | 185 °F | UL 746B |
| 可燃性(UL94) | HB @Thickness 0.710 mm |
HB @Thickness 0.0280 in |
UL 94 |
| V-1 @Thickness 1.21 mm |
V-1 @Thickness 0.0476 in |
UL 94 | |
| V-0 @Thickness 1.47 mm |
V-0 @Thickness 0.0579 in |
UL 94 | |
| 5VB @Thickness 2.00 mm |
5VB @Thickness 0.0787 in |
UL 94 | |
| 5VA @Thickness 3.40 mm |
5VA @Thickness 0.134 in |
UL 94 |