深圳热稳定PA66 408HS美国杜邦PA66408HS的价格
产品参数
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
吸水率 |
饱和(23℃) |
ASTM D-570 |
|
| DAM｜50%RH |
| 7.0｜- |
| % |
| 吸水率 |
24小时浸渍(23℃) |
ASTM D-570 |
|
| DAM｜50%RH |
| 1.2｜- |
| % |
| 物理性能 |
比重 |
|
ASTM D-792 |
|
| DAM｜50%RH |
| 1.09｜1.09 |
|
| 机械性能 |
断裂伸长率 |
23℃ |
ASTM D-638 |
|
| DAM｜50%RH |
| 80｜270 |
| % |
| 揉曲模量 |
23℃ |
ASTM D-790 |
|
| DAM｜50%RH |
| 1965｜1103 |
| MPa |
| 洛氏硬度M |
|
ASTM D-785 |
|
| DAM｜50%RH |
| M71｜M50 |
|
| 埃佐冲击强度 |
23℃ |
ASTM D-256 |
|
| DAM｜50%RH |
| 230｜240 |
| j/m |
| 硬度计硬度 |
|
ASTM D-676 |
|
| DAM｜50%RH |
| 83｜76 |
|
| 洛氏硬度R |
|
ASTM D-785 |
|
| DAM｜50%RH |
| R115｜R102 |
|
| 屈服伸长率 |
|
ASTM D-638 |
|
| DAM｜50%RH |
| 5｜15 |
| % |
| 屈服强度 |
23℃ |
|
|
| DAM｜50%RH |
| 60.7｜51.7 |
| MPa |
| 拉伸冲击强度 |
长试样23℃ |
ASTM D-1822 |
|
| DAM｜50%RH |
| 550｜1680 |
| KJ/m2 |
| 拉伸冲击强度 |
短试样23℃ |
ASTM D-1822 |
|
| DAM｜50%RH |
| 189｜265 |
| KJ/m2 |
| 拉伸强度 |
23℃ |
ASTM D-638 |
|
| DAM｜50%RH |
| 62.1｜51.7 |
| MPa |
| 电气性能 |
体积电阻率 |
|
ASTM D-257 |
|
| DAM｜50%RH |
| 1013｜1013 |
| Ω.cm |
| 介电常数 |
103Hz(cps) |
ASTM D-150 |
|
| DAM｜50%RH |
| 3.1｜4.8 |
|
| 耗散因数 |
100Hz(cps) |
ASTM D-150 |
|
| DAM｜50%RH |
| 0.02｜0.1 |
|
| 耗散因数 |
103Hz(cps) |
ASTM D-150 |
|
| DAM｜50%RH |
| 0.02｜0.11 |
|
| 耗散因数 |
106Hz(cps) |
ASTM D-150 |
|
| DAM｜50%RH |
| 0.02｜0.10 |
|
| 介电常数 |
100Hz(cps) |
ASTM D-150 |
|
| DAM｜50%RH |
| 3.1｜5.9 |
|
| 介电常数 |
106Hz(cps) |
ASTM D-150 |
|
| DAM｜50%RH |
| 2.9｜3.3 |
|
| 热性能 |
热畸变温度 |
(0.5)×106Pa |
ASTM D-648 |
|
| DAM｜50%RH |
| 230｜- |
| ℃ |
| UL可燃性导级 |
|
UL 94 |
|
| DAM｜50%RH |
| 94｜HB |
|
| 熔点结晶 |
|
ASTM D-2177 |
|
| DAM｜50%RH |
| 270｜- |
| ℃ |
| 线性热膨胀系数 |
|
ASTM D-696 |
|
| DAM｜50%RH |
| 7×10-5｜- |
| m/m/℃ |
| 荷重形变 |
13.8MPa，50℃ |
ASTM D-621 |
|
| DAM｜50%RH |
| 1.4｜- |
| % |
| 熔点 |
Fisher Johns法 |
ASTM D-789 |
|
| DAM｜50%RH |
| 255｜255 |
| ℃ |
| 热畸变温度 |
18×106Pa |
ASTM D-648 |
|
| DAM｜50%RH |
| 75｜- |
| ℃ |
| 脆化温度 |
|
ASTM D-746 |
|
| DAM｜50%RH |
| -104｜-84 |
| ℃ |
| 其它性能 |
需氧指数 |
|
ASTM D-2863 |
|
| DAM｜50%RH |
| 19｜20 |
深圳热稳定PA66 408HS美国杜邦PA66408HS的价格