重庆市瑞域工程塑料有限公司
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 物理性能 | 流动系数 | 300℃,1.2kg | ASTM D1238 | 10 | g/10min | |
| 比重 | ASTM D792 | 1.20 | ||||
| 吸水率 | ASTM D570 | 0.2 | % | |||
| 成型收缩率 | - | Parallel | ASTM D955 | 0.5-0.7 | % | |
| - | across | ASTM D955 | 0.5-0.7 | % | ||
| 机械性能 | 曲折率 | ASTM D542 | 1.585 | |||
| 引张强度 | 23℃ | ASTM D638 | 630 | kg/cm2 | ||
| 延伸率 | 降伏点 | 23℃ | ASTM D638 | 6 | % | |
| 破断点 | 23℃ | ASTM D638 | 110 | % | ||
| 弯曲强度 | 23℃ | ASTM D790 | 920 | kg/cm2 | ||
| 弯曲模量 | 23℃ | ASTM D790 | 24000 | kg/cm2 | ||
| Izod缺口冲击强度 | - | 1/4″ | ASTM D256 | 15 | Kg.cm/cm | |
| - | 1/8″ | ASTM D256 | 87 | Kg.cm/cm | ||
| 洛氏硬度 | ASTM D785 | 77 | M | |||
| 压缩强度 | ASTM D695 | 780 | kg/cm2 | |||
| 电气性能 | 体积电阻率 | ASTM D257 | 3 | ×1016Ωcm | ||
| 介电常数 | - | 60Hz | ASTM D150 | 2.95 | ||
| - | 106Hz | ASTM D150 | 2.9 | |||
| 绝缘破坏强度 | 1.6mm | ASTM D149 | 30 | KV/mm | ||
| 耐电弧性 | ASTM D495 | 110 | sec | |||
| 热性能 | 热变形温度 | - | 4.6kg/cm2 | ASTM D648 | 136 | ℃ |
| - | 18.6kg/cm2 | ASTM D648 | 125 | ℃ | ||
| 软化点温度 | ASTM D1525 | 148 | ℃ | |||
| 线膨胀系数 | 40-100℃ | ASTM D696 | 6-8 | ×105cm/cm/℃ | ||
| 热传导率 | ASTM C177 | 0.2 | W/m℃ | |||
| 阻燃性 | - | 1.5mm | UL94 | V-2 | ||
| - | 3.0mm | UL94 | V-2 | |||
| 光学性能 | 全光穿透率 | 3mm | ASTM D1003 | 89 | % | |
| 烛度 | ASTM D1003 | ＜0.8 | % | |||
透明 PC
透明 PC 比一般的 PC 多改进了一层透明性，具有优秀的流动性和热稳定性，是在高温中也几乎不会变色的材料。 再者，去除苯酚(PhOH)时，利用高真空降低 含量，对比其它树脂 模具定型明显低的特点。 这样的优点使其从 复杂的小型产品到大型注塑产品的注塑成型成为可能，也可扩大产品的设计范围。
特点- - 流动性
- - 高透明
- - UV 电阻
- - 杰出的高冲击强度
- - 优秀的易加工性适用于多种用途
- - 颜色多样化(Bluish, Greenish)
- - 车灯 (汽车前灯, 灯镜片), LGP, 建筑, CD, 光学镜片, 家具
扩散 PC
扩散 PC 是混合了高品质 PC 和微粒子成产的产品。本公司具备用于注塑和压缩的扩散 PC，使适用多种照明用途成为可能，同时也具备根据精确度和透明度的多种颜色群。
特点- - 使用绿色耐燃剂
- - 高透明 & 扩散性
- - UV 电阻
- - 生产率, 耐用性
- - LED照明/常规照明灯罩
注塑 |
数值 |
单位 |
建议干燥 |
是 |
- |
干燥温度 |
120 |
°C |
干燥时间，除湿干燥机 |
4 |
h |
加工前水分含量 |
≤0.2 |
% |
树脂温度（℃） |
260-280 |
°C |
模具温度 |
70-90 |
°C |
| 收缩率 | 0.4-0.6 | % |