ResinPBT310SE0阻燃V-0 沙伯基础310SE0
物理性能 | 比重 | ASTM D792, ISO 1183 | 1.40 | g/cm3 | |
特定体积 | ASTM D792 | 0.710 | cm3/g | ||
熔流率 | 250℃/2.16kg | ASTM D1238 | 8.6 | g/10 min | |
溶化体积流率 MVR | 250℃/2.16 kg |
ISO 1133 | 8.00 | cm3/10min | |
收缩率 | 流动 |
Internal Method | 1.1-1.8 | % | |
流动 |
Internal Method | 1.5-2.3 | % | ||
流动 |
Internal Method | 0.90-1.6 | % | ||
流动: 3.20 mm | Internal Method | 1.5-2.3 | % | ||
横向流动 |
Internal Method | 0.90-1.9 | % |
||
横向流动 | Internal Method | 1.0-1.7 | % | ||
横向流动 | Internal Method | 1.6-2.4 | % | ||
吸水率 | 饱和, 23℃ |
ISO 62 | 0.36 | % | |
平衡, 23℃, 50% RH |
ISO 62 | 0.080 | % | ||
洛氏硬度 | R 计秤 | ISO 2039-2 | 120 | ||
球压硬度 | H 358/30 | ISO 2039-1 | 105 | MPa | |
机械性能 | 拉伸模量 | -- | ASTM D638 | 2820 | MPa |
-- | ISO 527-2/1 | 2800 | MPa | ||
抗张强度 | 屈服 |
ASTM D638 | 58.0 | MPa | |
屈服 | ISO 527-2/50 | 55.0 | MPa | ||
断裂 |
ASTM D638 | 58.0 | MPa | ||
断裂 | ISO 527-2/50 | 40.0 | MPa | ||
伸长率 | 屈服 | ASTM D638 | 20 | % |
|
屈服 | ISO 527-2/50 | 6.0 | % |
||
断裂 | ASTM D638 | 20 | % |
||
断裂 | ISO 527-2/50 | 20 | % |
||
弯曲模量 | 50.0 mm 跨距 |
ASTM D790 | 2620 | MPa | |
-- |
ISO 178 | 2600 | MPa | ||
弯曲强度 | -- |
ISO 178 | 90.0 | MPa | |
屈服, 50.0 mm 跨距 |
ASTM D790 | 101 | MPa | ||
抗泰伯磨耗 | 1000 Cycles, 1000 g, CS-17 转轮 | Internal Method | 19.0 | mg |
|
简支梁缺口冲击强度 | -30℃ | ISO 179/1eA | 4.0 | kJ/m2 | |
23℃ | ISO 179/1eA | 8.0 | kJ/m2 | ||
23℃ | ISO 179/2C | 4.0 | kJ/m2 | ||
简支梁缺口冲击强度 | -30℃ |
ISO 179/1eU | 无断裂 | ||
23℃ | ISO 179/1eU | 无断裂 | |||
悬壁梁缺口冲击强度 | -30℃ |
ASTM D256 | 22 | J/m |
|
23℃ |
ASTM D256 | 37 | J/m |
||
-30℃ |
ISO 180/1A | 3.0 | kJ/m2 |
||
23℃ |
ISO 180/1A | 5.0 | kJ/m2 |
||
无缺口悬臂梁冲击 | 23℃ |
ASTM D4812 | 1600 | J/m |
|
-30℃ |
ISO 180/1U | 无断裂 | |||
23℃ | ISO 180/1U | 无断裂 | |||
装有测量仪表的落镖冲击 | 23℃, Energy at Peak Load |
ASTM D3763 | 200 | J | |
热性能 | 热变形温度 | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 162 | ℃ |
0.45 MPa, 未退火, 100 mm 跨距 |
ISO 75-2/Be | 135 | ℃ | ||
1.8 MPa, 未退火, 3.20 mm |
ASTM D648 | 74.0 | ℃ | ||
1.8 MPa, 未退火, 6.40 mm |
ASTM D648 | 71.0 | ℃ | ||
1.8 MPa, 未退火, 1000 mm 跨距 |
ISO 75-2/Ae | 60.0 | ℃ | ||
1.8 MPa, 未退火, 64.0 mm 跨距 |
ISO 75-2/Af | 71.0 | ℃ | ||
维卡软化温度 | -- | ASTM D1525 14, ISO 306/B50, ISO 306/B120 | 165 | ℃ | |
-- | ISO 306/A50 | 212 | ℃ | ||
Ball Pressure Test | 125℃ | IEC 60695-10-2 | pass | ||
线形膨胀系数 | 流动:-40到40℃ | ASTM E831 | 0.000079 | cm/cm/℃ | |
流动:60到138℃ |
ASTM E831 | 0.00013 | cm/cm/℃ | ||
横向:-40到40℃ | ISO 11359-2 | 0.000076 | cm/cm/℃ | ||
流动:23到60℃ |
ISO 11359-2 | 0.00010 | cm/cm/℃ | ||
横向:-40到40℃ |
ASTM E831 | 0.000079 | cm/cm/℃ | ||
横向:-40到40℃ |
ISO 11359-2 | 0.000073 | cm/cm/℃ | ||
横向:23到60℃ |
ISO 11359-2 | 0.00010 | cm/cm/℃ | ||
导热系数 | ISO 8302 | 0.24 | W/m/K |
||
电气性能 | 表面电阻率 | IEC 60093 | >1.0E 15 | ohms | |
体积电阻率 | IEC 60093 | >1.0E 15 | ohm·cm |
||
介电强度 | 1.60 mm, in Oil |
ASTM D149 | 22 | kV/mm |
|
3.20 mm, in Air |
ASTM D149 | 18 | kV/mm |
||
0.800 mm, 在油中 |
IEC 60243-1 | 31 | kV/mm |
||
1.00 mm |
IEC 60243-1 | 18 | kV/mm |
||
1.60 mm, 在油中 |
IEC 60243-1 | 24 | kV/mm |
||
3.20 mm, 在油中 |
IEC 60243-1 | 15 | kV/mm |
||
相对电容率 | 50 Hz |
IEC 60250 | 2.90 | ||
60 Hz |
IEC 60250 | 2.90 | |||
100 Hz |
IEC 60250 | 3.10 | |||
1 MHz |
IEC 60250 | 2.80 | |||
耗散因数 | 50 Hz |
IEC 60250 | 0.0010 | ||
60 Hz |
IEC 60250 | 0.0010 | |||
100 Hz | IEC 60250 | 0.0020 | |||
1 MHz | IEC 60250 | 0.010 | |||
耐电弧性 | (PLC) | ASTM D495 | PLC 6 | ||
漏电起痕指数 | -- |
IEC 60112 | 175 | V |
|
解决方案 B |
IEC 60112 | 100 | V |
||
可燃性 | UL 阻燃等级 | 0.710 mm |
UL 94 | V-0 | |
3.00 mm |
UL 94 | 5VA | |||
灼热丝易燃指数 | 1.00 mm | IEC 60695-2-12 | 960 | ℃ |
|
极限氧指数 | ISO 4589-2 | 30 | % |
长期供应PBT(饱和聚酯、聚对苯二甲酸丁酯)工程塑料、但不仅限于以下产品:增强PBT,环保PBT,阻燃PBT,PBT树脂,阻燃增强PBT,PBT塑料,PBT塑胶原料,无卤阻燃PBT,工程塑料PBT,美国GE PBT,PBT美国GE,PBT塑胶,PBT新料,阻燃环保PBT,玻纤增强PBT,加纤PBT供应PBT美国杜邦:SK602(玻纤增强15%),SK603(玻纤增强20%),SK605(玻纤增强30%),SK655(玻纤增强30%,阻燃),SK645FR(30%玻纤增强,阻燃V-0) 供应PBT美国GE:防火阻燃V-0级357、357M、357U、320SEO; 供应PBT美国GE:玻纤增强阻燃V-0级420SEO(30%)、DR48(17%)、DR51(15%); 供应PBT美国GE:310SEO、325、4022、4032、815、830; 供应PBT美国GE:1760E-BK1144、1102-BK1066、4521-BK1066、357U-BK1066、357U-1001; 供应PBT美国GE:364-GY8913、430-8433、430-BK1066、430-6187、434HR-BK1066; 供应PBT美国GE:508R-8433、508-1001、508-BK1066、K3501-1001、DR51-10; 供应PBT日本东丽:1101G-30、1401X06、1401X34、310SEO-1001、DR48-111、DR48-7001; 供应PBT台湾长春:阻燃V-0级4115、4815(玻纤15%),4120、4820(玻纤20%); 供应PBT台湾长春:阻燃V-0级4130、4830(玻纤30%),4140(玻纤40%); 供应PBT台湾长春:阻燃级1100-211M;一般级1100; 供应PBT日本宝理:玻纤增强难燃级70G15、70G20、70G30(GF15%、20%、30%); 供应PBT日本宝理:玻纤增强阻燃V-0级3116、3216、3226、3316(GF7.5、15%、20%、30%); 供应PBT日本三菱:5010GT15、5010GN1-30; 供应PBT德国巴斯夫:玻纤增强阻燃级B4406G4、B4406G6; 供应PBT德国巴斯夫:中粘度食品级B4500(FDA认证)。 PBT中文名称聚对苯二甲酸丁酯,简称饱和聚酯,系高结晶性热可塑性塑料。优点:1、机械性质安定抗张强度与抗张模数和尼龙相似;2、摩擦系数小有自润性; 3、吸水率低;4、电气性质优良;5、尺寸安定性良好;6、耐药品性、耐油性极佳。用途:1、电子电器:无熔线断电器、电磁开关、驰返变压器、家电把手、连接器、外壳等; 2、汽车:车门把手、保险杆、分电盘盖、挡泥板、导线护壳、轮圈盖等; 3、工业零件:OA风扇、键盘、钓具卷线器、零件、灯罩等。