产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | ||
| 基本性能 | 吸水率 | 24hrs | ASTM D-570 | 0.06 | % | |
| 物理性能 | 模具收缩率 | 3.2mm | ASTM D-955 | 1.4 | 10-3 | |
| 比重 | ASTM D-792 | 1.31 | ||||
| 增强 | 30 | % | ||||
| 阻燃性 | UL 94 | 1.5 | mm | |||
| 阻燃性 | UL 94 | V-1 | ||||
| 机械性能 | 拉伸强度 | 屈服点 | 3.2mm | ASTM D-638 | 121 | MPa |
| 断裂点 | 3.2mm | ASTM D-638 | 5 | MPa | ||
| 弯曲模量 | 6.4mm | ASTM D-790 | 7786 | MPa | ||
| 缺口冲击强度 | -40°C | ASTM D-256 | 96 | J/M | ||
| 弯曲强度 | 6.4mm | ASTM D-790 | 172 | MPa | ||
| 缺口冲击强度 | 23°C | ASTM D-256 | 117 | J/M | ||
| 洛氏硬度 | ASTM D-785 | 108 | ||||
| 电气性能 | 介电常数 | 60Hz | ASTM D-150 | 3.15 | ||
| 损耗因数 | 60Hz | ASTM D-150 | 0.002 | |||
| 热性能 | UL长期使用温度 | 电气 | UL 746B | 110 | °C | |
| 含冲击 | UL 746B | 105 | °C | |||
| 无冲击 | UL 746B | 110 | °C | |||
| 热变形温度 | 0.45MPa | ASTM D-648 | 140 | °C | ||
| 热变形温度 | 1.8MPa | ASTM D-648 | 135 | °C | ||
| 线膨胀系数 | ASTM E-831 | 2.5×10-5 | 1/°C | |||
![%1NN8F7T]{{HMB49TIRB%PE_副本_副本_](https://cbu01.alicdn.com/img/ibank/2014/407/738/1850837704_919536740.jpg)
![OS)7{7E]V{@IXZ(L8(~49DN](https://cbu01.alicdn.com/img/ibank/2014/613/853/1853358316_919536740.jpg)
|
||||||||||
|
|
我们的态度 质量决定成败、服务成就未来
如购买的材料有任何不满意，想退换， 随时联系客服
购买的材料到贵司发现材料购买有误，第一时间联系客服。包邮退回
从选材、设计到成型，正逢塑料都是您"产品制造"的好帮手。 正逢超级工程塑料 新时代的追求 |
• 材料的预干燥条件为80~100℃、1~2个小时。
• 为了防止树脂分解，请按下列条件设定树脂温度及机筒内的滞留时间。
加工温度：260 ～290 ℃ 不得超过330度
料筒温度 |
滞留时间 |
260℃ |
60分钟以内 |
290 ℃ |
30分钟以内 |
上述为参考值，随条件而变 |
|
建议在100～150℃范围内设定PPO的模具温度。模具温度处于80℃时通常没有问题，但如果存在光泽、表面光洁度等外观问题时，建议使用高模温