Ultramid® A3EG6
聚酰胺66
30% 玻璃纤维增强材料
产品说明：
Ultramid A3EG6 is a 30% glass fiber reinforced injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability.
Applications
Typical applications include such as lamp socket housings, cooling fans, insulating profiles for aluminium window frames, and electrical insulation parts.
Ultramid® A3EG6 物性表
| 基本信息 |
|
| 黄卡编号 |
|
| 填料/增强材料 |
|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| RoHS 合规性 |
|
| 形式 |
|
| 加工方法 |
|
| 多点数据 |
Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2) |
| 物理性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 比重 |
1.36 |
-- |
g/cm3 |
ASTM D792, ISO 1183 |
| 溶化体积流率（MVR） (275°C/5.0 kg) |
40.0 |
-- |
cm3/10min |
ISO 1133 |
| 收缩率 - 流动 (3.18 mm) |
0.30 |
-- |
% |
|
| 吸水率 |
|
|
|
|
| 饱和 |
5.5 |
-- |
% |
ASTM D570 |
| 饱和, 23°C |
5.5 |
-- |
% |
ISO 62 |
| 平衡, 50% RH |
1.7 |
-- |
% |
ASTM D570 |
| 平衡, 23°C, 50% RH |
1.7 |
-- |
% |
ISO 62 |
| 机械性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 拉伸模量 (23°C) |
10000 |
7200 |
MPa |
ISO 527-2 |
| 抗张强度 |
|
|
|
|
| 断裂, 23°C |
186 |
-- |
MPa |
ASTM D638 |
| 断裂, -40°C |
238 |
227 |
MPa |
ISO 527-2 |
| 断裂, 23°C |
190 |
130 |
MPa |
ISO 527-2 |
| 伸长率 |
|
|
|
|
| 断裂, 23°C |
3.0 |
-- |
% |
ASTM D638 |
| 断裂, 23°C |
3.0 |
5.0 |
% |
ISO 527-2 |
| 弯曲模量 (23°C) |
8600 |
6500 |
MPa |
ISO 178 |
| 弯曲应力 (23°C) |
280 |
210 |
MPa |
ISO 178 |
| 冲击性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 简支梁缺口冲击强度 |
|
|
|
ISO 179 |
| -30°C |
11 |
-- |
kJ/m2 |
ISO 179 |
| 23°C |
13 |
22 |
kJ/m2 |
ISO 179 |
| 简支梁无缺口冲击强度 |
|
|
|
ISO 179 |
| -30°C |
70 |
-- |
kJ/m2 |
ISO 179 |
| 23°C |
85 |
100 |
kJ/m2 |
ISO 179 |
| 悬壁梁缺口冲击强度 |
|
|
|
ASTM D256 |
| -40°C |
91 |
-- |
J/m |
ASTM D256 |
| 23°C |
110 |
-- |
J/m |
ASTM D256 |
| 热性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 载荷下热变形温度 |
|
|
|
|
| 0.45 MPa, 未退火 |
250 |
-- |
°C |
ASTM D648, ISO 75-2/B |
| 1.8 MPa, 未退火 |
250 |
-- |
°C |
ASTM D648, ISO 75-2/A |
| 熔融峰值温度 |
260 |
-- |
°C |
ASTM D3418, ISO 3146 |
| 线形热膨胀系数 |
|
|
|
|
| 流动 |
1.0E-5 |
-- |
cm/cm/°C |
ASTM E831 |
| 流动 |
2.5E-5 |
-- |
cm/cm/°C |
|
| 横向 |
6.5E-5 |
-- |
cm/cm/°C |
|
| RTI Elec |
|
|
|
UL 746 |
| 0.750 mm |
120 |
-- |
°C |
UL 746 |
| 1.50 mm |
120 |
-- |
°C |
UL 746 |
| 3.00 mm |
120 |
-- |
°C |
UL 746 |
| 6.00 mm |
120 |
-- |
°C |
UL 746 |
| RTI Imp |
|
|
|
UL 746 |
| 1.50 mm |
120 |
-- |
°C |
UL 746 |
| 3.00 mm |
120 |
-- |
°C |
UL 746 |
| 6.00 mm |
120 |
-- |
°C |
UL 746 |
| RTI |
|
|
|
UL 746 |
| 1.50 mm |
130 |
-- |
°C |
UL 746 |
| 3.00 mm |
130 |
-- |
°C |
UL 746 |
| 6.00 mm |
130 |
-- |
°C |
UL 746 |
| 电气性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 体积电阻率 |
|
|
|
|
| 1.50 mm |
1.0E+13 |
1.0E+10 |
ohms·cm |
ASTM D257 |
| -- |
1.0E+13 |
1.0E+10 |
ohms·cm |
IEC 60093 |
| 介电常数 (1 MHz) |
3.50 |
5.60 |
|
IEC 60250 |
| 耗散因数 |
|
|
|
IEC 60250 |
| 100 Hz |
0.014 |
0.23 |
|
IEC 60250 |
| 1 MHz |
0.014 |
0.16 |
|
IEC 60250 |
| 漏电起痕指数 |
550 |
550 |
V |
IEC 60112 |
| 可燃性 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| UL 阻燃等级 |
|
|
|
UL 94 |
| 1.50 mm |
HB |
-- |
|
UL 94 |
| 3.00 mm |
HB |
-- |
|
UL 94 |
| 6.00 mm |
HB |
-- |
|
UL 94 |
| 注射 |
干燥 |
单位制 |
|
| 干燥温度 |
80.0 |
°C |
|
| 干燥时间 |
2.0 到 4.0 |
hr |
|
| 建议的最大水分含量 |
0.15 |
% |
|
| 加工（熔体）温度 |
280 到 305 |
°C |
|
| 模具温度 |
80.0 到 90.0 |
°C |
|
| 注塑压力 |
3.50 到 12.5 |
MPa |
|
| 注射速度 |
快速 |
|
|