Nilit Nilamid A3 H G10 50% Glass Reinforced PA66
Polymer,Thermoplastic,Nylon,Nylon 66,Nylon 66, 50% Glass Fiber Filled
Nilit
产品说明:
Description: Nilamid A3 H G10 (50% Glass Reinforced) is a high strength material, that is used for structural applications. It is easy to mould, and shows outstanding stiffness and creep resistance, even at elevated temperatures. It is used for highly loaded applications like high torque transmission housings, electrical cable holders and tensioners of ski bindings.
Key characteristics:
High stiffness
High strength
Good impact strength
Excellent thermal performance
Good creep resistance
Information provided by NILIT.
ilit Nilamid A3 H G10 50% Glass Reinforced PA66 物性表
物理性能 |
额定值 (公制) |
额定值 (英制) |
测试方法 |
密度 |
1.57 g/cc |
0.0567 lb/in3 |
ASTM D792, ISO 1183 |
吸水率 |
0.50 % |
0.50 % |
23°C, 24h in H2O; sim. ISO 62 |
饱和吸水率 |
3.5 % |
3.5 % |
sim. ISO 62 |
线性成型收缩率,Flow |
0.0020 cm/cm |
0.0020 in/in |
Euronil |
线性成型收缩率,横向 |
0.0030 cm/cm |
0.0030 in/in |
Euronil |
机械性能 |
额定值 (公制) |
额定值 (英制) |
测试方法 |
抗张强度(屈服) |
220 MPa |
31900 psi |
ISO 527, ASTM D638 |
伸长率 (断裂) |
2.0 % |
2.0 % |
ISO 527, ASTM D638 |
拉伸模量 |
16.5 GPa |
2390 ksi |
ISO 527, ASTM D638 |
弯曲强度 |
310 MPa |
45000 psi |
ISO 178, ASTM D790 |
|
230 MPa @Temperature 90.0 °C |
33400 psi @Temperature 194 °F |
ISO 178, ASTM D790 |
弯曲模量 |
15.0 GPa |
2180 ksi |
ISO 178, ASTM D790 |
|
9.50 GPa @Temperature 90.0 °C |
1380 ksi @Temperature 194 °F |
ISO 178, ASTM D790 |
如需 完整物性表及 SGS报告MSDS报告UL黄卡COA出厂报告请联系我索取