SABIC HDPE FI1157 产品说明：
SABIC HDPE CC862 is high density polyethylene specially developed for still water bottle caps that meet organoleptic properties requirements. The material offers an ideal combination of rigidity, impact strength and low warpage properties.
Typical Applications
Caps & Closures for the packaging of still mineral water
Caps & Closures for beverage food and industrial packaging
Special Features
Good organoleptics properties
Complies with food contacts regulations
Slip agent free grade
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.963 | g/cm3 | ASTM D1505 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| 抗环境应力开裂 (100% Igepal, 模压成型, F50) | 3.00 | hr | ASTM D1693B |
| 硬度 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D, 注塑) | 62 | ASTM D2240 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 抗张强度 | ASTM D638 | ||
| 屈服, 注塑 | 26.0 | MPa | ASTM D638 |
| 断裂, 注塑 | 18.0 | MPa | ASTM D638 |
| 伸长率 (断裂, 注塑) | > 800 | % | ASTM D638 |
| 弯曲模量 (注塑) | 1000 | MPa | ASTM D790 |
| 弯曲强度 (注塑) | 25.0 | MPa | ASTM D790 |
HDPE特性：
高密度聚乙烯具有良好的耐热性和耐寒性，化学稳定性好，还具有较高的刚性和韧性，机械强度好。介电性能，耐环境应力开裂性亦较好。硬度、拉伸强度和蠕变性优于低密度聚乙烯；耐磨性、电绝缘性、韧性及耐寒性均较好，但与低密度绝缘性比较略差些；化学稳定性好，在室温条件下，不溶于任何有机溶剂，耐酸、碱和各种盐类的腐蚀；薄膜对水蒸气和空气的渗透性小、吸水性低；耐老化性能差，耐环境开裂性不如低密度聚乙烯，特别是热氧化作用会使其性能下降，所以，树脂需加入抗氧剂和紫外线吸收剂等来提高改善这方面的不足。高密度聚乙烯薄膜在受力情况下的热变形温度较低，这一点应用时要注意。
应用：用于挤出包装薄膜，绳索，编织袋，渔网，水管；注塑低档日用品及外壳，非承载荷构件，胶箱，周转箱；挤出吹塑容器，中空制品，瓶子。
基本特性：高密度聚乙烯是一种不透明白色腊状材料，比重比水轻，比重为0.941~0.960，柔软而且有韧性，但比LDPE略硬，也略能伸长，无毒，无味
。
燃烧特性：易燃，离火后能继续燃烧，火焰上端呈黄色，下端呈蓝色，燃烧时会熔融，有液体滴落，无黑烟冒出，同时，发出石蜡燃烧时发出的气味。
主要优点：耐酸碱，耐有机溶剂，电绝缘性优良，低温时，仍能保持一定的韧性。表面硬度，拉伸强度，刚性等机械强度都高于LDPE，接近于PP，比PP韧，但表面光洁度不如PP。
主要缺点：机械性能差，透气差，易变形，易老化，易发脆，脆性低于PP，易应力开裂，表面硬度低，易刮伤。难印刷，印刷时，需进行表面放电处理，不能电镀，表面无光泽。