SABIC HDPE F00952 产品说明：
SABIC® HDPE F00952 resin is a high molecular weight high density polyethylene copolymer which has been designed specifically for blown film extrusion. Its high molecular weight, broad molecular distribution and high density combine succesfully to give excellent extrudability with high film strength and rigidity. The material contains anti oxidant .
| 物理性能 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 密度 | 0.952 | g/cm3 | ISO 1183 |
| 熔流率（熔体流动速率） | ISO 1133 | ||
| 190°C/2.16 kg | 0.050 | g/10 min | ISO 1133 |
| 190°C/21.6 kg | 9.0 | g/10 min | ISO 1133 |
| 薄膜 | 额定值 | 单位制 | 测试方法 |
|---|---|---|---|
| 薄膜厚度 - 经测试 | 15 | μm | |
| 割线模量 | ASTM D882 | ||
| MD : 15 μm, 吹塑薄膜 | 1250 | MPa | ASTM D882 |
| TD : 15 μm, 吹塑薄膜 | 1500 | MPa | ASTM D882 |
| 抗张强度 | ASTM D882 | ||
| MD : 屈服, 15 μm, 吹塑薄膜 | 33.0 | MPa | ASTM D882 |
| TD : 屈服, 15 μm, 吹塑薄膜 | 31.0 | MPa | ASTM D882 |
| MD : 断裂, 15 μm, 吹塑薄膜 | 60.0 | MPa | ASTM D882 |
| TD : 断裂, 15 μm, 吹塑薄膜 | 56.0 | MPa | ASTM D882 |
| 伸长率 | ASTM D882 | ||
| MD : 断裂, 15 μm, 吹塑薄膜 | 400 | % | ASTM D882 |
| TD : 断裂, 15 μm, 吹塑薄膜 | 550 | % | ASTM D882 |
| 落锤冲击 (15 μm, 吹塑薄膜) | 180 | g | ASTM D1709 |
| 埃尔曼多夫抗撕强度 | ASTM D1922 | ||
| MD : 15 μm, 吹塑薄膜 | 12 | g | ASTM D1922 |
| TD : 15 μm, 吹塑薄膜 | 60 | g | ASTM D1922 |
基本特性：高密度聚乙烯是一种不透明白色腊状材料，比重比水轻，比重为0.941~0.960，柔软而且有韧性，但比LDPE略硬，也略能伸长，无毒，无味
。
燃烧特性：易燃，离火后能继续燃烧，火焰上端呈黄色，下端呈蓝色，燃烧时会熔融，有液体滴落，无黑烟冒出，同时，发出石蜡燃烧时发出的气味。
主要优点：耐酸碱，耐有机溶剂，电绝缘性优良，低温时，仍能保持一定的韧性。表面硬度，拉伸强度，刚性等机械强度都高于LDPE，接近于PP，比PP韧，但表面光洁度不如PP。
主要缺点：机械性能差，透气差，易变形，易老化，易发脆，脆性低于PP，易应力开裂，表面硬度低，易刮伤。难印刷，印刷时，需进行表面放电处理，不能电镀，表面无光泽。
主要用途：
高密度聚乙烯树脂可采用注射、挤出、吹塑和旋转成型等方法成型塑料制品。采用注射成型可成型出各种类型的容器、工业配件、医用品、玩具、壳体、瓶塞和护罩等制品。采用吹塑成型可成型各种中空容器、超薄型薄膜等。采用挤出成型可成型管材、拉伸条带、捆扎带、单丝、电线和电缆护套等。
另外，还可成型建筑用装饰板、百叶窗、合成木材、合成纸、合成膜和成型钙塑制品等 。