余姚市福邦塑化有限公司
产品参数
70G33L
80G33L
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 基本性能 | 吸水率 | 24小时浸渍(23℃) | ASTM D-570 | 0.7 | % |
| 吸水率 | 饱和(23℃) | ASTM D-570 | 5.4 | % | |
| 物理性能 | 比重 | ASTM D-792 | 1.38 | ||
| 机械性能 | 洛氏硬度M | DAM | ASTM D-785 | M101 | |
| 拉伸强度 | 23℃,DAM | ASTM D-638 | 196.1 | MPa | |
| 埃佐冲击强度 | 23℃,50%RH | ASTM D-256 | 133 | j/m | |
| 埃佐冲击强度 | 23℃,DAM | ASTM D-256 | 107 | j/m | |
| 断裂伸长率 | 23℃,DAM | ASTM D-638 | 3 | % | |
| 挠曲模量 | 23℃,50%RH | ASTM D-790 | 6205 | MPa | |
| 挤剪强度 | 23℃,DAM | ASTM D-732 | 86 | MPa | |
| 挠曲模量 | 23℃,DAM | ASTM D-790 | 8963 | ||
| 挠曲强度 | 23℃,DAM | ASTM D-790 | 262 | MPa | |
| 拉伸强度 | 23℃,50%RH | ASTM D-638 | 124.1 | MPa | |
| 泰伯磨耗量 | 50%RH | 14 | cycles | ||
| 断裂伸长率 | 23℃,50%RH | ASTM D-638 | 4 | % | |
| 电气性能 | 介电强度 | DAM | ASTM D-149 | 530 | volts/mil |
| 介电强度 | (分步法) | ASTM D-149 | 440 | volts/mil | |
| 体积电阻率 | 100%RH | ASTM D-257 | 109 | ohm-cm | |
| 体积电阻率 | DAM | ASTM D-257 | 1015 | ohm-cm | |
| 介电常数 | DAM@103Hz赫 | ASTM D-150 | 4.5 | ||
| 介电常数 | 100%RH@106Hz赫 | ASTM D-150 | 10.7 | ||
| 损耗因数 | DAM@103Hz赫 | ASTM D-150 | 0.02 | ||
| 介电常数 | 100%RH@103Hz赫 | ASTM D-150 | 25.0 | ||
| 损耗因数 | 100%RH@106Hz赫 | ASTM D-150 | 0.02 | ||
| 介电常数 | DAM@106Hz赫 | ASTM D-150 | 3.7 | ||
| 热性能 | 热畸变温度 | 1.8MPa | ASTM D-648 | 249 | ℃ |
| 线性热膨胀系数 | ASTM D-696 | 2.3×10-5 | m/m/℃ | ||
| 熔点 | DAM | ASTM D-789 | 255 | ℃ | |
| 熔点 | 50%RH | ASTM D-789 | 255 | ℃ | |
| 性能项目 | 试验条件[状态] | 测试方法 | 干燥 | 调节后的 | 数据单位 | |
| 物理性能 | 比重 | ASTM D792 | 1.33 | g/cm3 | ||
| ISO 1183 | 1.32 | g/cm3 | ||||
| 收缩率 | 流动:3.20mm | Internal Method | 0.40 | % | ||
| 横向流动:3.20mm | Internal Method | 1.2 | % | |||
| 横向流量: 2.00 mm | ISO 294-4 | 0.80 | % | |||
| 流量: 2.00 mm | ISO 294-4 | 0.30 | % | |||
| 吸水率 | 23℃,24hr | ISO 62 | 0.83 | % | ||
| 机械性能 | 拉伸模量 | 23℃ | ISO 527-2 | 8700 | 5800 | MPa |
| 拉伸应力 | 断裂, 23℃ | ISO 527-2 | 142 | 95.0 | MPa | |
| 23℃ | ASTM D638 | 145 | 110 | MPa | ||
| 断张率 | 23℃ | ISO 527-2 | 4.0 | 5.0 | % | |
| 弯曲模量 | 23℃ | ASTM D790 | 6900 | 5070 | MPa | |
| 23℃ | ISO 178 | 7400 | 5200 | MPa | ||
| 简支梁缺口冲击强度 | -40℃ | ISO 179/1eA | 13 | 13 | kJ/m2 | |
| 23℃ | ISO 179/1eA | 20 | 22 | kJ/m2 | ||
| 简支梁缺口冲击强度 | 23℃ | ISO 179/1eU | 91 | 80 | kJ/m2 | |
| 悬臂梁缺口冲击强度 | 23℃ | ASTM D256 | 220 | 240 | J/m | |
| -40℃ | ISO 180/1A | 15 | 10 | kJ/m2 | ||
| -30℃ | ISO 180/1A | 14 | 10 | kJ/m2 | ||
| 23℃ | ISO 180/1A | 21 | 20 | kJ/m2 | ||
| 热性能 | 热变形温度 | 0.45 MPa, 未退火 | ISO 75-2/B | 262 | ℃ | |
| 1.8 MPa, 未退火 | ASTM D648 | 250 | ℃ | |||
| 1.8 MPa, 未退火 | ISO 75-2/A | 247 | ℃ | |||
| 熔融温度 | ISO 11357-3 | 262 | ℃ | |||
| ASTM D3418 | 263 | ℃ | ||||
| RTI Ele | 0.75mm | UL 746 | 120 | ℃ | ||
| 1.50mm | UL 746 | 120 | ℃ | |||
| 3.00mm | UL 746 | 120 | ℃ | |||
| RTI Imp | 0.75mm | UL 746 | 65 | ℃ | ||
| 1.50mm | UL 746 | 105 | ℃ | |||
| 3.00 mm | UL 746 | 105 | ℃ | |||
| RTI Str | 0.75mm | UL 746 | 85 | ℃ | ||
| 1.50mm | UL 746 | 95 | ℃ | |||
| 3.00mm | UL 746 | 105 | ℃ | |||
| 电气性能 | 相比耐漏电其痕指数 | 3.00mm | UL 746 | 600 | V | |
| 漏电其痕指数 | 3.00mm | IEC 60112 | PLC 0 | |||
| 可燃性 | UL阻燃等级 | 0.750mm | IEC 60695-11-10，-20 | HB | ||
| 1.50mm | IEC 60695-11-10，-20 | HB | ||||
| 3.00mm | IEC 60695-11-10，-20 | HB | ||||
| 灼热丝易燃指数 | 0.750mm | IEC 60695-2-12 | 650 | ℃ | ||
| 1.50mm | IEC 60695-2-12 | 650 | ℃ | |||
| 3.00mm | IEC 60695-2-12 | 775 | ℃ | |||
| 热灯丝点火温度 | 0.750mm | IEC 60695-2-13 | 675 | ℃ | ||
| 1.50mm | IEC 60695-2-13 | 675 | ℃ | |||
| 3.00mm | IEC 60695-2-13 | 725 | ℃ | |||
| 极限氧指数 | ISO 4589-2 | 23 | % | |||