苏州友群塑化有限公司
产品参数
| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 熔点 | MCI方法 | 237 | ℃ | |
| 熔融指数(260℃,5kg) | ASTM D-1238 | 26 | g/10min | ||
| 密度 | ASTM D-1505 | 0.833 | g/cm3 | ||
| 机械性能 | 弹性强度 | ASTM D-790 | 48 | MPa | |
| Izod耐冲击强度 | ASTM D-256 | 11 | KJ/m2 | ||
| 屈服拉伸强度 | ASTM D-638 | 26 | MPa | ||
| 弹性模量 | ASTM D-790 | 1570 | MPa | ||
| 拉伸模量 | ASTM D-638 | 1765 | MPa | ||
| Rockwell硬度 | ASTM D-785 | R88 | |||
| 拉伸强度 | ASTM D-638 | 20 | MPa | ||
| 断裂伸长率 | ASTM D-638 | 32 | % | ||
| 电气性能 | 体积电阻系数 | ASTM D-257 | >1016 | Ωcm | |
| 吸水率(24hr) | ASTM D-570 | 0.01 | % | ||
| 介电强度 | ASTM D-149 | 65 | KV/mm | ||
| 介电常数(100～1MHz) | ASTM D-150 | 2.12 | |||
| 介电消散因子(23℃,1MHz) | ASTM D-150 | 0.0002 | |||
| 热性能 | 模收缩率(纵向/横向) | MCI方法 | 2.1/1.7 | % | |
| Vicat软化点 | ASTM D-1525 | 176 | ℃ | ||
| 热变形温度(4.6kg/cm2) | ASTM D-648 | 90 | ℃ | ||
| 热传导系数 | ASTM BS-847A | 4*10-4 | calcm/seccm2℃ | ||
| 线形膨胀系数 | ASTM D-696 | 1.17*10-4 | 1/℃ | ||
| 比热 | ASTM C-351 | 0.47 | cal/g℃ | ||
| 燃烧速率 | ASTM D-635 | 2.54 | cm/min | ||
| 其它性能 | 折射率 | ASTM D-542 | 1.463 | nd | |
| 透光率 | ASTM D-1746 | 94 | % | ||
| 模糊度 | ASTM D-1746 | 1.1 | % | ||