Plexar® PX1164

乙烯醋酸乙烯共聚物

LyondellBasell Industries

产品说明:

Plexar tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resins and copolymers, EVA, EMA, polypropylene, polyamide (nylon), ethylene vinyl alcohol copolymers (EVOH), ionomer and other sealants, polyethylene terephthalate (PET) resins and copolymers, styrenic polymers, metal, and paperboard. Product grades primarily used for blown and cast films, sheet and thermoforming, blow molding, extrusion coating and lamination, tubing, pipe, and other specialty applications are available in pellet form. Contact your Plexar sales and/or Equistar technical service representative for more information and specific recommendations for your application(s).

供货地区	北美洲 拉丁美洲 欧洲 亚太地区
用途	包装 薄膜 工业应用 粘合剂 粘结树脂
机构评级	FDA 21 CFR 175.105
形式	粒子
加工方法	薄膜挤出 吹塑薄膜 挤出

物理性能	额定值	单位制	测试方法
密度	0.928	g/cm3	ASTM D1505
熔流率（熔体流动速率） (190°C/2.16 kg)	3.8	g/10 min	ASTM D1238

薄膜	额定值	单位制	测试方法
抗张强度			ASTM D882
MD : 屈服, 2.0 mil, 吹塑薄膜	609	psi
TD : 屈服, 2.0 mil, 吹塑薄膜	1070	psi
MD : 断裂, 2.0 mil, 吹塑薄膜	3520	psi
TD : 断裂, 2.0 mil, 吹塑薄膜	3950	psi
伸长率			ASTM D882
MD : 屈服, 2.0 mil, 吹塑薄膜	14	%
TD : 屈服, 2.0 mil, 吹塑薄膜	28	%
MD : 断裂, 2.0 mil, 吹塑薄膜	710	%
TD : 断裂, 2.0 mil, 吹塑薄膜	460	%
埃尔曼多夫抗撕强度			ASTM D1922
MD : 2.0 mil, 吹塑薄膜	94	g
TD : 2.0 mil, 吹塑薄膜	420	g
水气透过率 (100% RH, 2.0 mil, 吹塑薄膜)

乙烯-醋酸乙烯共聚物简称EVA，一般醋酸乙烯（VA）含量在5%～40%。与聚乙烯相比，EVA[1]由于在分子链中引入了醋酸乙烯单体，从而降低了高结晶度，提高了柔韧性、抗冲击性、填料相溶性和热密封性能，被广泛应用于发泡鞋料、功能性棚膜、包装膜、热熔胶、电线电缆及玩具等领域。

如未找到您合适的型号,或者有工程技术方面的疑问，欢迎来电来人至我公司咨询,本公司工作人员竭诚为您服务!

邓生手机:15995594155

电话:0512-53128920

传真:0512-53128921

Q  Q:3378023070

邮箱:hc15995594155@126.com

Plexar EVA PX1007 工业应用 包装用 食品级 挤出级 流动率3.1 LyondellBasell Industries

Plexar EVA PX1164 粘结树脂 粘合剂用 工业应用 包装用 食品级 挤出级 流动率3.8 LyondellBasell Industries

Plexar EVA PX5125 包装薄膜用 工业应用 食品级 挤出级 流动率6 LyondellBasell Industries