苏州海财塑化有限公司
HANWHA EVA 2319
乙烯醋酸乙烯共聚物
Hanwha Chemical
产品说明:
HANWHA EVA 2319 is manufactured by Dow tubular high pressure process and designed for variety of foam molding application such as shoes and sandals etc.. EVA 2319 is well known for its excellent processability and high quality assurance.
· Excellent Foam Molding Property
· Very Good Mechanical Properties
· Excellent Loading Property of Various Fillers
· Good Elastic Property of Sponge
| 供货地区 |
|
|||
| 添加剂 |
|
|||
| 特性 |
|
|||
| 用途 |
|
|||
| 形式 |
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 密度 |
0.939 |
g/cm3 |
ASTM D1505 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) |
2.5 |
g/10 min |
ASTM D1238 |
| 醋酸乙烯含量 |
19.0 |
wt% |
内部方法 |
| 硬度 |
额定值 |
单位制 |
测试方法 |
| 肖氏硬度 |
|
|
ASTM D2240 |
| 邵氏 A |
90 |
|
|
| 邵氏 D |
36 |
|
|
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 抗张强度 (断裂) |
1990 |
psi |
ASTM D638 |
| 伸长率 (断裂) |
800 |
% |
ASTM D638 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 脆化温度 |
< -105 |
°F |
ASTM D746 |
| 维卡软化温度 |
|
|
|
乙烯-醋酸乙烯共聚物简称EVA，一般醋酸乙烯（VA）含量在5%～40%。与聚乙烯相比，EVA[1]由于在分子链中引入了醋酸乙烯单体，从而降低了高结晶度，提高了柔韧性、抗冲击性、填料相溶性和热密封性能，被广泛应用于发泡鞋料、功能性棚膜、包装膜、热熔胶、电线电缆及玩具等领域。
如未找到您合适的型号,或者有工程技术方面的疑问，欢迎来电来人至我公司咨询,本公司工作人员竭诚为您服务!
邓生手机:15995594155
电话:0512-53128920
传真:0512-53128921
Q Q:3378023070
邮箱:hc15995594155@126.com
HANWHA EVA 2020 抗结块 光滑 加增滑剂 高透明 抗氧化 农业应用 薄膜应用 流动率0.5 醋酸乙烯含量3.5 Hanwha Chemical
HANWHA EVA 2030 抗结块 光滑 加增滑剂 高透明 抗氧化 农业应用 薄膜应用 流动率0.8 醋酸乙烯含量6.5 Hanwha Chemical
HANWHA EVA 2040 高透明 抗氧化 食品级 农业应用 薄膜应用 流动率0.8 醋酸乙烯含量9.5 Hanwha Chemical
HANWHA EVA 2050 高透明 抗氧化 食品级 农业应用 薄膜应用 流动率1 醋酸乙烯含量12 Hanwha Chemical
HANWHA EVA 2240 良好的稳定性 良好的热封性 薄膜挤出 包装用 流动率2 醋酸乙烯含量9.5 Hanwha Chemical
HANWHA EVA 2250 光学性能 高透明 抗氧化 食品级 薄膜挤出 包装用 流动率2 醋酸乙烯含量12 Hanwha Chemical
HANWHA EVA 2315 可发泡 共聚物 鞋类用 流动率1.8 醋酸乙烯含量15 硬度98A Hanwha Chemical
HANWHA EVA 2319 抗氧化 可发泡 共聚物 鞋类用 流动率2.5 醋酸乙烯含量19 硬度90A Hanwha Chemical
EVA PE E032A 抗氧化 抗结块 增滑剂 高强度 农业应用 吹塑薄膜用 流动率0.5 醋酸乙烯含量3 硬度43D Hanwha Total Petrochemical Co., Ltd.
EVA PE E060A 抗氧化 抗结块 增滑剂 高强度 农业应用 吹塑薄膜用 流动率0.8 醋酸乙烯含量6 硬度41D Hanwha Total Petrochemical Co., Ltd.