Orevac® T 9305

乙烯醋酸乙烯共聚物

Arkema

产品说明:

OREVAC® T 9305 is a random terpolymer of ethylene, vinyl acetate and maleic anhydride made by high-pressure radicalar polymerization process. As an ethylene copolymer, OREVAC® T 9305 is compatible with PE in all proportions, and with most other ethylene copolymers. Vinyl acetate brings softness, flexibility and polarity, maleic anhydride gives reactivity, leading to versatile adhesive properties to polar and non polar substrates.

Applications
OREVAC® T 9305 is compatible with most tackifying resins and waxes and can be used for hot melt adhesives formulations. OREVAC® T 9305 is also suitable to produce thermo-adhesive films for solid substrates like PA, PET & PU films, aluminium foils...

供货地区	北美洲 非洲和中东 拉丁美洲 欧洲 亚太地区
特性	良好粘结性 三元共聚物
用途	粘合剂

物理性能	额定值	单位制	测试方法
密度	0.951	g/cm3	ISO 1183, ASTM D1505
熔流率（熔体流动速率） (190°C/2.16 kg)	150 到 210	g/10 min	ASTM D1238, ISO 1133
醋酸乙烯含量	26.0 到 30.0	wt%
Maleic Anhydride Content	6400	ppm
硬度	额定值	单位制	测试方法
肖氏硬度 (邵氏 A, 15 秒, 0.110 in, 模压成型)	75		ASTM D2240, ISO 868

机械性能	额定值	单位制	测试方法
抗张强度
断裂, 0.110 in, 模压成型 2	798	psi	ASTM D638
断裂, 0.110 in, 模压成型	798	psi	ISO 527-2/5A/50
伸长率
断裂, 0.110 in, 模压成型 2	700 到 900	%	ASTM D638
断裂, 0.110 in, 模压成型

 

 

乙烯-醋酸乙烯共聚物简称EVA，一般醋酸乙烯（VA）含量在5%～40%。与聚乙烯相比，EVA[1]由于在分子链中引入了醋酸乙烯单体，从而降低了高结晶度，提高了柔韧性、抗冲击性、填料相溶性和热密封性能，被广泛应用于发泡鞋料、功能性棚膜、包装膜、热熔胶、电线电缆及玩具等领域。

如未找到您合适的型号,或者有工程技术方面的疑问，欢迎来电来人至我公司咨询,本公司工作人员竭诚为您服务!

邓生手机:15995594155

电话:0512-53128920

传真:0512-53128921

Q  Q:3378023070

邮箱:hc15995594155@126.com

Orevac EVA 18211 流延薄膜 粘合剂 良好粘结性 吹塑薄膜 共挤出成型 片材挤出成型 流动率3.5 Arkema

Orevac EVA 9309 三元共聚物 流延薄膜用 流动率4 硬度70D Arkema

Orevac EVA 9314 三元共聚物 吹塑薄膜用 流动率2 硬度55D Arkema

Orevac EVA T 9304 粘结树脂 三元共聚物 吹塑薄膜用 高清晰 薄膜挤出 流动率25.5-9.3 醋酸乙烯含量23.5-26.5 硬度82A Arkema

Orevac EVA T 9305 粘合剂用 良好粘结性 三元共聚物 流动率150-210 醋酸乙烯含量26-30 硬度75A Arkema

Orevac EVA T 9307 Y 三元共聚物 高清晰 良好粘结性 流动率9.5-12 醋酸乙烯含量13-15 硬度91A Arkema

Orevac EVA T 9318 高清晰 电线电缆应用 粘结树脂用 流延薄膜 吹塑薄膜 共挤出成型 三元共聚物 流动率6-8 醋酸乙烯含量17-20 硬度88A Arkema