苏州海财塑化有限公司
HANWHA EVA 2250
乙烯醋酸乙烯共聚物
Hanwha Chemical
产品说明:
HANWHA EVA 2250 is manufactured by DOW tubular high pressure process and designed for variety of film application such as flexible package. EVA 2250 has well balanced property of high clarity, mechanical property and processability.
- Good Optical Property
- Good Mechanical Property
- Excellent Processability
| 供货地区 |
|
|||
| 添加剂 |
|
|||
| 特性 |
|
|||
| 用途 |
|
|||
| 机构评级 |
FDA 21 CFR 177.1350(a)(1) |
|||
| 形式 |
|
|||
| 加工方法 |
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 密度 |
0.931 |
g/cm3 |
ASTM D1505 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) |
2.0 |
g/10 min |
ASTM D1238 |
| 醋酸乙烯含量 |
12.0 |
wt% |
内部方法 |
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 抗张强度 (断裂) |
2750 |
psi |
ASTM D638 |
| 伸长率 (断裂) |
800 |
% |
ASTM D638 |
| 薄膜 |
额定值 |
单位制 |
测试方法 |
| 薄膜厚度 - 经测试 |
2.4 |
mil |
|
| 抗张强度 |
|
|
ASTM D882 |
| MD : 断裂, 2.4 mil |
3840 |
psi |
|
| TD : 断裂, 2.4 mil |
3360 |
psi |
|
| 伸长率 |
|
|
ASTM D882 |
| MD : 断裂, 2.4 mil |
280 |
% |
|
| TD : 断裂, 2.4 mil |
700 |
% |
|
| 落锤冲击 (2.4 mil) |
|
|
|
乙烯-醋酸乙烯共聚物简称EVA，一般醋酸乙烯（VA）含量在5%～40%。与聚乙烯相比，EVA[1]由于在分子链中引入了醋酸乙烯单体，从而降低了高结晶度，提高了柔韧性、抗冲击性、填料相溶性和热密封性能，被广泛应用于发泡鞋料、功能性棚膜、包装膜、热熔胶、电线电缆及玩具等领域。
如未找到您合适的型号,或者有工程技术方面的疑问，欢迎来电来人至我公司咨询,本公司工作人员竭诚为您服务!
邓生手机:15995594155
电话:0512-53128920
传真:0512-53128921
Q Q:3378023070
邮箱:hc15995594155@126.com
HANWHA EVA 1529 热融胶用 粘合剂用 抗氧化 食品级 流动率400 醋酸乙烯含量28 硬度64A Hanwha Chemical
HANWHA EVA 1533 热融胶用 粘合剂用 抗氧化 流动率25 醋酸乙烯含量33 硬度69A Hanwha Chemical
HANWHA EVA 1540 热融胶用 粘合剂用 抗氧化 流动率60 醋酸乙烯含量40 硬度54A Hanwha Chemical
HANWHA EVA 1626 Hanwha Chemical
HANWHA EVA 1628 Hanwha Chemical
HANWHA EVA 1633 Hanwha Chemical
HANWHA EVA 1815 电线电缆应用 高弹性 抗氧化 流动率6 醋酸乙烯含量15 硬度93A Hanwha Chemical
HANWHA EVA 1826 共聚物 电线电缆应用 高弹性 抗氧化 流动率4.5 醋酸乙烯含量26 硬度82A Hanwha Chemical
HANWHA EVA 1828 共聚物 电线电缆应用 高弹性 抗氧化 流动率4 醋酸乙烯含量28 硬度79A Hanwha Chemical
HANWHA EVA 1834 光滑 加增滑剂 电线电缆应用 高弹性 抗氧化 流动率18 醋酸乙烯含量33 硬度65A Hanwha Chemical