苏州海财塑化有限公司
Ultrathene® UE672
乙烯醋酸乙烯共聚物
LyondellBasell Industries
产品说明:
ULTRATHENE UE 672 is an EVA copolymer with excellent impact strength, heat sealability, good toughness and flexibility. Applications may include flexible packaging films for food and healthcare, as well as liquid and heavy duty packaging and pallet stretch film. UE 672 contains antioxidant and high levels of slip and antiblock additives.
| 供货地区 |
|
|||
| 添加剂 |
|
|||
| 特性 |
|
|||
| 用途 |
|
|||
| 机构评级 |
|
|||
| 形式 |
|
|||
| 加工方法 |
|
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) |
0.45 |
g/10 min |
ASTM D1238 |
| 醋酸乙烯含量 |
12.5 |
wt% |
|
| 薄膜 |
额定值 |
单位制 |
测试方法 |
| 薄膜厚度 - 经测试 |
1.5 |
mil |
|
| 割线模量 |
|
|
ASTM D882 |
| 1% 正割, MD : 1.5 mil |
11700 |
psi |
|
| 1% 正割, TD : 1.5 mil |
12900 |
psi |
|
| 抗张强度 |
|
|
ASTM D882 |
| MD : 屈服, 1.5 mil |
1640 |
psi |
|
| TD : 屈服, 1.5 mil |
810 |
psi |
|
| MD : 断裂, 1.5 mil |
5620 |
psi |
|
| TD : 断裂, 1.5 mil |
4670 |
psi |
|
| 伸长率 |
|
|
ASTM D882 |
| MD : 屈服, 1.5 mil |
59 |
% |
|
| TD : 屈服, 1.5 mil |
10 |
% |
|
| MD : 断裂, 1.5 mil |
470 |
% |
|
| TD : 断裂, 1.5 mil |
650 |
% |
|
| 埃尔曼多夫抗撕强度 |
|
|
ASTM D1922 |
| MD : 1.5 mil |
56 |
g |
|
| TD : 1.5 mil |
150 |
g |
|
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 脆化温度 |
-105 |
°F |
ASTM D746 |
| 维卡软化温度 |
176 |
°F |
ASTM D1525 |
| 熔融温度 |
|
|
|
乙烯-醋酸乙烯共聚物简称EVA，一般醋酸乙烯（VA）含量在5%～40%。与聚乙烯相比，EVA[1]由于在分子链中引入了醋酸乙烯单体，从而降低了高结晶度，提高了柔韧性、抗冲击性、填料相溶性和热密封性能，被广泛应用于发泡鞋料、功能性棚膜、包装膜、热熔胶、电线电缆及玩具等领域。
如未找到您合适的型号,或者有工程技术方面的疑问，欢迎来电来人至我公司咨询,本公司工作人员竭诚为您服务!
邓生手机:15995594155
电话:0512-53128920
传真:0512-53128921
Q Q:3378023070
邮箱:hc15995594155@126.com
Tritheva EVA PN 2021 低收缩性 耐化学品 高ESCR 抗应力开裂 管道系统用 鞋类用 家具用 型材用 流动率2.1 醋酸乙烯含量17.7-20.3 硬度87A Petroquimica Triunfo
Tritheva EVA TN 2007 食品级 耐冲击 尺寸稳定 高透明 涂覆应用 共挤出成型 薄膜挤出级 流动率0.65 醋酸乙烯含量9-11 Petroquimica Triunfo
Tritheva EVA TN 2020 涂覆应用 食品级 热稳定 高透明 共挤出成型 薄膜挤出级 流动率2 醋酸乙烯含量8-9 Petroquimica Triunfo
Tritheva EVA TN 8093 高分子量 耐冲击 尺寸稳定 食品级 高透明 农业应用 层压板 共挤出成型 薄膜挤出级 流动率0.4 醋酸乙烯含量11-13 Petroquimica Triunfo