Orevac® 18211

乙烯醋酸乙烯共聚物

Arkema

产品说明:

OREVAC® 18211 is a coextrusion adhesive resin based on a maleic anhydride modified ethylene-vinyl acetate copolymer. It is available in pellet form for use in conventional extrusion and coextrusion equipment designed to process polyolefin.

Applications
OREVAC® 18211 has been designed to develop a reliable bonding strength in coextrusion processes between polyethylene or ethylene copolymers and different materials among which polyamides, PS, EVOH and PET. It can be processed within different extrusion and coextrusion technologies including cast film, blown film, sheet calandering, blow molding, tube extrusion.

供货地区	北美洲 非洲和中东 拉丁美洲 欧洲 亚太地区
特性	共聚物 良好粘结性
用途	Blown Film 薄膜 吹塑成型应用 管件 流延薄膜 片材 粘合剂
形式	粒子
加工方法	吹塑薄膜 吹塑成型 共挤出成型 挤出 流延薄膜 片材挤出成型 压延

物理性能	额定值	单位制	测试方法
密度	0.950	g/cm3	ISO 1183, ASTM D1505
熔流率（熔体流动速率） (190°C/2.16 kg)	3.5	g/10 min	ASTM D1238, ISO 1133

热性能	额定值	单位制	测试方法
维卡软化温度	124	°F	ISO 306/A, ASTM D1525 2
熔融温度

乙烯-醋酸乙烯共聚物简称EVA，一般醋酸乙烯（VA）含量在5%～40%。与聚乙烯相比，EVA[1]由于在分子链中引入了醋酸乙烯单体，从而降低了高结晶度，提高了柔韧性、抗冲击性、填料相溶性和热密封性能，被广泛应用于发泡鞋料、功能性棚膜、包装膜、热熔胶、电线电缆及玩具等领域。

如未找到您合适的型号,或者有工程技术方面的疑问，欢迎来电来人至我公司咨询,本公司工作人员竭诚为您服务!

邓生手机:15995594155

电话:0512-53128920

传真:0512-53128921

Q  Q:3378023070

邮箱:hc15995594155@126.com

Orevac EVA 18211 流延薄膜 粘合剂 良好粘结性 吹塑薄膜 共挤出成型 片材挤出成型 流动率3.5 Arkema

Orevac EVA 9309 三元共聚物 流延薄膜用 流动率4 硬度70D Arkema

Orevac EVA 9314 三元共聚物 吹塑薄膜用 流动率2 硬度55D Arkema

Orevac EVA T 9304 粘结树脂 三元共聚物 吹塑薄膜用 高清晰 薄膜挤出 流动率25.5-9.3 醋酸乙烯含量23.5-26.5 硬度82A Arkema

Orevac EVA T 9305 粘合剂用 良好粘结性 三元共聚物 流动率150-210 醋酸乙烯含量26-30 硬度75A Arkema

Orevac EVA T 9307 Y 三元共聚物 高清晰 良好粘结性 流动率9.5-12 醋酸乙烯含量13-15 硬度91A Arkema

Orevac EVA T 9318 高清晰 电线电缆应用 粘结树脂用 流延薄膜 吹塑薄膜 共挤出成型 三元共聚物 流动率6-8 醋酸乙烯含量17-20 硬度88A Arkema