苏州海财塑化有限公司
Bynel® 39E660
乙烯醋酸乙烯共聚物
DuPont Packaging & Industrial Polymers
产品说明:
BYNEL® Series 3900 resins are anhydride-modified ethylene vinyl acetate polymers. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to process polyethylene (PE) resins.
BYNEL 3900 series resins are most often used to adhere to EVA, EVOH, ionomer, polyamide and PE.
| 产品说明 |
||||
| BYNEL® Series 3900 resins are anhydride-modified ethylene vinyl acetate polymers. They are available in pellet form for use in conventional extrusion and coextrusion equipment designed to process polyethylene (PE) resins. |
||||
| 总体 |
|
|||
| 供货地区 |
|
|||
| 特性 |
· 良好粘结性 |
|||
| 用途 |
· 粘合剂 |
|||
| 机构评级 |
|
|||
| 形式 |
· 粒子 |
|||
| 加工方法 |
|
|||
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 比重 |
|
|
|
| -- |
0.942 |
|
ASTM D792 |
| -- |
0.940 |
g/cm3 |
ISO 1183 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) |
2.5 |
g/10 min |
ASTM D1238, ISO 1133 |
| 热性能 |
额定值 |
单位制 |
测试方法 |
| 维卡软化温度 |
162 |
°F |
ASTM D1525, ISO 306 |
| 溶融温度（DSC） |
|
|
|
乙烯-醋酸乙烯共聚物简称EVA，一般醋酸乙烯（VA）含量在5%～40%。与聚乙烯相比，EVA[1]由于在分子链中引入了醋酸乙烯单体，从而降低了高结晶度，提高了柔韧性、抗冲击性、填料相溶性和热密封性能，被广泛应用于发泡鞋料、功能性棚膜、包装膜、热熔胶、电线电缆及玩具等领域。
如未找到您合适的型号,或者有工程技术方面的疑问，欢迎来电来人至我公司咨询,本公司工作人员竭诚为您服务!
邓生手机:15995594155
电话:0512-53128920
传真:0512-53128921
Q Q:3378023070
邮箱:hc15995594155@126.com
Bynel EVA 3126 良好粘结性 挤出成型 粘合剂用 FDA食品级 流动率8.1 DuPont Packaging & Industrial Polymers
Bynel EVA 3810 挤出成型 FDA食品级 流动率2.6 DuPont Packaging & Industrial Polymers
Bynel EVA 3860 挤出成型 FDA食品级 流动率5.7 DuPont Packaging & Industrial Polymers
Bynel EVA 3861 挤出成型 FDA食品级 流动率2 DuPont Packaging & Industrial Polymers
Bynel EVA 3930 良好粘结性 挤出成型 FDA食品级 流动率0.85 DuPont Packaging & Industrial Polymers
Bynel EVA 39E660 良好粘结性 挤出成型 FDA食品级 流动率2.5 DuPont Packaging & Industrial Polymers
Bynel EVA E418 加增滑剂 挤出成型 FDA食品级 流动率11 DuPont Packaging & Industrial Polymers