苏州海财塑化有限公司
Braskem EVA TN2006
乙烯醋酸乙烯共聚物
Braskem
产品说明:
TN2006 is an Ethylene-Vinyl Acetate (EVA) copolymer with good mechanical properties, high flexibility and toughness even with low temperature, excellent optical and salability properties. Additionally, this product has good water vapor barrier. The melt properties allow processability in tubular film equipment, being able to be coextruded in combination with many others materials
| 产品说明 |
||||
| TN2006 is an Ethylene-Vinyl Acetate (EVA) copolymer with good mechanical properties, high flexibility and toughness even with low temperature, excellent optical and salability properties. Additionally, this product has good water vapor barrier. The melt properties allow processability in tubular film equipment, being able to be coextruded in combination with many others materials |
||||
| 总体 |
|
|||
| 材料状态 |
|
|||
| 添加剂 |
|
|||
| 特性 |
|
|||
| 用途 |
|
|||
| 机构评级 |
|
|||
| 加工方法 |
|
|||
| 物理性能 |
额定值 |
单位制 |
测试方法 |
| 密度 |
0.940 |
g/cm3 |
ASTM D1505 |
| 熔流率（熔体流动速率） (190°C/2.16 kg) |
0.70 |
g/10 min |
ASTM D1238 |
| 醋酸乙烯含量 |
18.0 |
wt% |
|
| 硬度 |
额定值 |
单位制 |
测试方法 |
| 肖氏硬度 |
|
|
ASTM D2240 |
| 邵氏 A, 模压成型 |
89 |
|
|
| 邵氏 D, 模压成型 |
39 |
|
|
| 机械性能 |
额定值 |
单位制 |
测试方法 |
| 抗张强度 (断裂, 模压成型) |
4790 |
psi |
ASTM D638 |
| 伸长率 (断裂, 模压成型) |
680 |
% |
ASTM D638 |
| 薄膜 |
额定值 |
单位制 |
测试方法 |
| 薄膜厚度 - 经测试 |
2.0 |
mil |
|
| 割线模量 |
|
|
ASTM D882 |
| 2% 正割, MD : 2.0 mil, 吹塑薄膜 |
5660 |
psi |
|
| 2% 正割, TD : 2.0 mil, 吹塑薄膜 |
5510 |
psi |
|
| 抗张强度 |
|
|
ASTM D882 |
| MD : 断裂, 2.0 mil, 吹塑薄膜 |
4640 |
psi |
|
| TD : 断裂, 2.0 mil, 吹塑薄膜 |
4500 |
psi |
|
| 伸长率 |
|
|
ASTM D882 |
| MD : 断裂, 2.0 mil, 吹塑薄膜 |
450 |
% |
|
| TD : 断裂, 2.0 mil, 吹塑薄膜 |
700 |
% |
|
| 落锤冲击 (2.0 mil, 吹塑薄膜) |
600 |
g |
ASTM D1709B |
| 埃尔曼多夫抗撕强度 |
|
|
ASTM D1922 |
| MD : 2.0 mil, 吹塑薄膜 |
150 |
g |
|
| TD : 2.0 mil, 吹塑薄膜 |
|
|
|
乙烯-醋酸乙烯共聚物简称EVA，一般醋酸乙烯（VA）含量在5%～40%。与聚乙烯相比，EVA[1]由于在分子链中引入了醋酸乙烯单体，从而降低了高结晶度，提高了柔韧性、抗冲击性、填料相溶性和热密封性能，被广泛应用于发泡鞋料、功能性棚膜、包装膜、热熔胶、电线电缆及玩具等领域。
如未找到您合适的型号,或者有工程技术方面的疑问，欢迎来电来人至我公司咨询,本公司工作人员竭诚为您服务!
邓生手机:15995594155
电话:0512-53128920
传真:0512-53128921
Q Q:3378023070
邮箱:hc15995594155@126.com
Braskem EVA 3019 PE 耐疲劳 高弹性 沥青改性用 薄膜用 鞋类用 粘合剂用 高抗应力开裂 流动率2.5 VAC含量19 硬度90A
Braskem EVA CN8092 抗氧化 无卤 流延薄膜用 母料用 流动率8.5 VAC含量15.5 硬度91A
Braskem EVA HM 2528 低分子量 高抗应力开裂 涂层应用 粘合剂用 挤出 注射成型 流动率25 硬度79A
Braskem EVA HM728F 低速凝固晶点 低温热封 低硬度 耐低温 吹塑薄膜 流延薄膜 抗氧化 流动率6 VAC含量28 硬度80A
Braskem EVA PN2021 抗氧化 高抗应力开裂 收缩性低 耐化学性 食品级 管件用 玩具用 型材用 鞋类用 流动率2.1 VAC含量19 硬度89A
Braskem EVA TN2005 高光 高清晰度 高分子量 农业应用 吹塑薄膜 包装用 流动率0.5 VAC含量13.5 硬度91A
Braskem EVA TN2006 光学性能用 食品包装 土工膜 层压板用 拉伸缠绕膜 共挤薄膜 低温韧性 流动率0.7 VAC含量18 硬度89A
Braskem EVA TN2020 可焊接 抗穿孔性 高光 高清晰度 食品包装用 收缩性薄膜用 包装用 流动率2 VAC含量8.5 硬度93A
Braskem EVA VA4018R 耐疲劳 耐磨损 可交联 抗氧化 体育用品用 流动率4 VAC含量18 硬度69A
Braskem EVA VA8010SUV 流动率8 VAC含量19 硬度85A