CompaMid® PA 6 GF 30 HY
聚酰胺6
30% 玻璃纤维增强材料
产品说明：
Our new crosslinkable CompaMid® PA 6 compounds are thermoplastic polymers which behave like elastomers over a wide temperature range as a result of beta radiation cross-linking. Thanks to crosslinking, the originally thermoplastic material can withstand significantly higher temperatures of up to 350 °C, thus providing greater shape retention under thermal load. Due to its excellent performance profile, crosslinkable CompaMid® PA 6 can replace costly high-performance plastics such as PPA, PPS or LCP in many cases. No mould changes are required when switching from standard PA 6 to CompaMid® PA 6, and the process parameters also remain the same.
Electrical Applications
Thanks to their outstanding electrical and mechanical properties, crosslinkable CompaMid® PA 6 compounds are ideally suited for applications in the electrical and electronics industries.
Automotive Applications
Crosslinked components made of CompaMid® PA 6 are used in the engine bay and exhaust system, where requirements are the toughest for heat resistance and shape retention, as well as resistance to salts, chemicals and corrosive media.
CompaMid® PA 6 GF 30 HY 物性表
| 基本信息 |
|
| 填料/增强材料 |
· 玻璃纤维增强材料, 30% 填料按重量 |
| 特性 |
· 可交联 · 良好的电气性能 · 耐水解性 |
| 物理性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 密度 |
1.35 |
-- |
g/cm3 |
ISO 1183 |
| 收缩率 1 |
|
|
|
ISO 294-4 |
| 垂直流动方向 : 80°C |
0.55 |
-- |
% |
ISO 294-4 |
| 流动方向 : 80°C |
0.10 |
-- |
% |
ISO 294-4 |
| 吸水率 |
|
|
|
ISO 62 |
| 饱和, 23°C |
7.0 |
-- |
% |
ISO 62 |
| 平衡, 23°C, 50% RH |
2.0 |
-- |
% |
ISO 62 |
| 粘数 |
150 |
-- |
cm3/g |
ISO 307 |
| 机械性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 拉伸模量 |
10000 |
6500 |
MPa |
ISO 527-2/1 |
| 拉伸应力 |
|
|
|
ISO 527-2/50 |
| 屈服 |
185 |
110 |
MPa |
ISO 527-2/50 |
| 断裂 |
170 |
-- |
MPa |
ISO 527-2/50 |
| 拉伸应变 |
|
|
|
ISO 527-2/50 |
| 屈服 |
3.0 |
5.5 |
% |
ISO 527-2/50 |
| 断裂 |
3.0 |
-- |
% |
ISO 527-2/50 |
| 冲击性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 简支梁缺口冲击强度 |
|
|
|
ISO 179/1eA |
| -30°C |
9.0 |
-- |
kJ/m2 |
ISO 179/1eA |
| 23°C |
12 |
-- |
kJ/m2 |
ISO 179/1eA |
| 简支梁无缺口冲击强度 |
|
|
|
ISO 179/1eU |
| -30°C |
73 |
-- |
kJ/m2 |
ISO 179/1eU |
| 23°C |
93 |
-- |
kJ/m2 |
ISO 179/1eU |
| 热性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 热变形温度 |
|
|
|
|
| 1.8 MPa, 未退火 |
205 |
-- |
°C |
ISO 75-2/A |
| 8.0 MPa, 未退火 |
135 |
-- |
°C |
ISO 75-2/C |
| 维卡软化温度 |
220 |
-- |
°C |
ISO 306/B120 |
| 熔融温度 |
222 |
-- |
°C |
ISO 11357-3 |
| 线形热膨胀系数 |
|
|
|
ISO 11359-2 |
| 流动 : 23 到 80°C |
1.0E-5 到 3.0E-5 |
-- |
cm/cm/°C |
ISO 11359-2 |
| 横向 : 23 到 80°C |
1.0E-4 到 1.2E-4 |
-- |
cm/cm/°C |
ISO 11359-2 |
| Heat Distortion |
|
|
°C |
|
| 电气性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 表面电阻率 |
1.0E+10 |
-- |
ohms |
IEC 60093 |
| 体积电阻率 |
1.0E+15 |
-- |
ohms·cm |
IEC 60093 |
| 介电强度 (1.00 mm) |
40 |
-- |
kV/mm |
IEC 60243-1 |
| 相对电容率 (1 MHz) |
3.80 |
-- |
|
IEC 60250 |
| 漏电起痕指数 (解决方案 A) |
575 |
-- |
V |
IEC 60112 |
| 可燃性 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| UL 阻燃等级 (0.800 mm) |
HB |
-- |
|
UL 94 |
如未找到您合适的型号,或者有工程技术方面的疑问，欢迎来电来人至我公司咨询,本公司工作人员竭诚为您服务!
邓生手机:15995594155
电话:0512-53128920
传真:0512-53128921
Q Q:3378023070
邮箱:hc15995594155@126.com
CompaMid PA 6 CI 耐低温冲击 可交联 良好的电气性能 V-2 树脂 DimeLika Plast GmbH 尼龙6
CompaMid PA 6 GF 10 M 20 可交联 良好的电气性能 加10%玻纤 矿物20%填料 DimeLika Plast GmbH 尼龙6
CompaMid PA 6 GF 15 可交联 良好的电气性能 加15%玻纤 DimeLika Plast GmbH 尼龙6
CompaMid PA 6 GF 25 可交联 良好的电气性能 加25%玻纤 DimeLika Plast GmbH 尼龙6
CompaMid PA 6 GF 30 HI 高抗撞击 加30%玻纤 DimeLika Plast GmbH 尼龙6
CompaMid PA 6 GF 30 HY 耐水解 可交联 加30%玻纤 DimeLika Plast GmbH 尼龙6
CompaMid PA 6 GF 30 可交联 良好的电气性能 加30%玻纤 DimeLika Plast GmbH 尼龙6
CompaMid PA 6 GF 50 可交联 良好的电气性能 加50%玻纤 DimeLika Plast GmbH 尼龙6
CompaMid PA 6 GK 30 可交联 良好的电气性能 玻璃珠30%填料 DimeLika Plast GmbH 尼龙6
CompaMid PA 6 HI 高抗撞击 V-2 DimeLika Plast GmbH 尼龙6