Ashley Polymers Ashlene® 630-25G Nylon 6, 25% Glass Reinforced
Polymer,Thermoplastic,Nylon,Nylon 6,Nylon 6, 30% Glass Fiber Filled
Ashley Polymers
产品说明:
Nylon 6, 25% glass reinforced resin.
Data provided by the manufacturer
Ashley Polymers Ashlene® 630-25G Nylon 6, 25% Glass Reinforced 物性表
| 物理性能 |
额定值 (公制) |
额定值 (英制) |
测试方法 |
| 密度 |
1.30 g/cc |
0.0470 lb/in3 |
ASTM D792 |
| 吸水率 |
1.1 % |
1.1 % |
24 hrs; ASTM D570 |
| 线性成型收缩率 |
0.0050 cm/cm |
0.0050 in/in |
ASTM D955 |
| 机械性能 |
额定值 (公制) |
额定值 (英制) |
测试方法 |
| 洛氏硬度（R 级） |
119 |
119 |
ASTM D785 |
| 极限抗拉强度 |
145 MPa |
21000 psi |
ATSM D638 |
| 伸长率 (断裂) |
3.0 % |
3.0 % |
ASTM D638 |
| 屈服伸长率 |
3.0 % |
3.0 % |
ASTM D638 |
| 弯曲强度 |
241 MPa |
35000 psi |
ASTM D790 |
| 弯曲模量 |
6.70 GPa |
972 ksi |
ASTM D790 |
| 悬壁梁缺口冲击强度 |
1.12 J/cm |
2.10 ft-lb/in |
ASTM D256 |
| 热性能 |
额定值 (公制) |
额定值 (英制) |
测试方法 |
| 熔融温度 |
216 °C |
421 °F |
ASTM D3418 |
| 载荷下热变形温度(0.46 MPa) |
216 °C |
421 °F |
ASTM D648 |
| 载荷下热变形温度(1.8 MPa) |
215 °C |
419 °F |
ASTM D648 |
尼龙（聚酰胺）是最早且应用最广泛的热塑性工程塑料。具有强韧、耐磨、耐冲击、耐疲
劳、耐腐蚀、耐油等优异性能。经过60 多年的发展，世界尼龙产量接近600 万t，成为五大工程塑料中产量最大
、用途最广、品种最多的重要的高分子材料但尼龙,尤其是PA6 存在低温和干态冲击性能差、吸水率大等弱点。为
适应工业发展的需要，使其向高冲击、低吸水和优化加工等方向发展的研究成为广泛关注的课题。在很多应用领
域中，对尼龙的韧性有更高的要求，因此对PA6进行增韧改性具有重要的理论和实际意义。美国、西欧和日本先后
开发了各种牌号的高抗冲击性尼龙6 合金（超韧尼龙）。其中具有代表性的有Du Pont公司的Zytel-ST系列...
如未找到您合适的型号,或者有工程技术方面的疑问，欢迎来电来人至我公司咨询,本公司工作人员竭诚为您服务!
邓生手机:15995594155
电话:0512-53128920
传真:0512-53128921
Q Q:3378023070
邮箱:hc15995594155@126.com
ASHLENE 尼龙6 塑胶原料 PA6 626SB 纯树脂 热稳定 挤出 Ashley Polymers, Inc.
ASHLENE 尼龙6 塑胶原料 PA6 630-13G 尺寸稳定 玻纤13%增强 Ashley Polymers, Inc.
ASHLENE 尼龙6 塑胶原料 PA6 630-25G 玻纤25%增强 Ashley Polymers, Inc.
ASHLENE 尼龙6 塑胶原料 PA6 630-33G 玻纤33%增强 Ashley Polymers, Inc.
ASHLENE 尼龙6 塑胶原料 PA6 630-33GU 玻纤33%增强 热稳定 Ashley Polymers, Inc.
ASHLENE 尼龙6 塑胶原料 PA6 630BU 注塑用 黑色纯树脂 Ashley Polymers, Inc.
ASHLENE 尼龙6 塑胶原料 PA6 734LD 高抗冲击 Ashley Polymers, Inc.
ASHLENE 尼龙6 塑胶原料 PA6 734-SP5 高抗冲击 Ashley Polymers, Inc.
ASHLENE 尼龙6 塑胶原料 PA6 735LD 冲击改性 Ashley Polymers, Inc.