苏州海财塑化有限公司
聚酰胺6
50% 玻璃纤维增强材料
DimeLika Plast GmbH
产品说明：
Our new crosslinkable CompaMid® PA 6 compounds are thermoplastic polymers which behave like elastomers over a wide temperature range as a result of beta radiation cross-linking. Thanks to crosslinking, the originally thermoplastic material can withstand significantly higher temperatures of up to 350 °C, thus providing greater shape retention under thermal load. Due to its excellent performance profile, crosslinkable CompaMid® PA 6 can replace costly high-performance plastics such as PPA, PPS or LCP in many cases. No mould changes are required when switching from standard PA 6 to CompaMid® PA 6, and the process parameters also remain the same.
Electrical Applications
Thanks to their outstanding electrical and mechanical properties, crosslinkable CompaMid® PA 6 compounds are ideally suited for applications in the electrical and electronics industries.
Automotive Applications
Crosslinked components made of CompaMid® PA 6 are used in the engine bay and exhaust system, where requirements are the toughest for heat resistance and shape retention, as well as resistance to salts, chemicals and corrosive media.
CompaMid® PA 6 GF 50 物性表
| 基本信息 |
|
| 填料/增强材料 |
· 玻璃纤维增强材料, 50% 填料按重量 |
| 特性 |
· 可交联 · 良好的电气性能 |
| 物理性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 密度 |
1.55 |
-- |
g/cm³ |
ISO 1183 |
| 收缩率 1 |
|
|
|
ISO 294-4 |
| 垂直流动方向 : 80°C |
0.50 |
-- |
% |
ISO 294-4 |
| 流动方向 : 80°C |
0.050 |
-- |
% |
ISO 294-4 |
| 吸水率 |
|
|
|
ISO 62 |
| 饱和, 23°C |
5.0 |
-- |
% |
ISO 62 |
| 平衡, 23°C, 50% RH |
1.5 |
-- |
% |
ISO 62 |
| 粘数 |
150 |
-- |
cm³/g |
ISO 307 |
| 机械性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 拉伸模量 |
16000 |
11000 |
MPa |
ISO 527-2/1 |
| 拉伸应力 |
|
|
|
ISO 527-2/50 |
| 屈服 |
230 |
145 |
MPa |
ISO 527-2/50 |
| 断裂 |
210 |
160 |
MPa |
ISO 527-2/50 |
| 拉伸应变 |
|
|
|
ISO 527-2/50 |
| 屈服 |
2.5 |
4.5 |
% |
ISO 527-2/50 |
| 断裂 |
2.5 |
5.5 |
% |
ISO 527-2/50 |
| 冲击性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 简支梁缺口冲击强度 |
|
|
|
ISO 179/1eA |
| -30°C |
11 |
12 |
kJ/m² |
ISO 179/1eA |
| 23°C |
15 |
25 |
kJ/m² |
ISO 179/1eA |
| 简支梁无缺口冲击强度 |
|
|
|
ISO 179/1eU |
| -30°C |
85 |
90 |
kJ/m² |
ISO 179/1eU |
| 23°C |
90 |
95 |
kJ/m² |
ISO 179/1eU |
| 热性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 热变形温度 |
|
|
|
|
| 1.8 MPa, 未退火 |
210 |
-- |
°C |
ISO 75-2/A |
| 8.0 MPa, 未退火 |
170 |
-- |
°C |
ISO 75-2/C |
| 熔融温度 |
222 |
-- |
°C |
ISO 11357-3 |
| 线形热膨胀系数 |
|
|
|
ISO 11359-2 |
| 流动 : 23 到 80°C |
1.0E-5 到 2.5E-5 |
-- |
cm/cm/°C |
ISO 11359-2 |
| 横向 : 23 到 80°C |
9.0E-5 到 1.1E-4 |
-- |
cm/cm/°C |
ISO 11359-2 |
| Heat Distortion |
|
|
°C |
|
| 电气性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 表面电阻率 |
1.0E+10 |
-- |
ohms |
IEC 60093 |
| 体积电阻率 |
1.0E+15 |
-- |
ohms·cm |
IEC 60093 |
| 介电强度 (1.00 mm) |
40 |
-- |
kV/mm |
IEC 60243-1 |
| 相对电容率 (1 MHz) |
4.20 |
-- |
|
IEC 60250 |
| 漏电起痕指数 (解决方案 A) |
575 |
-- |
V |
IEC 60112 |
| 可燃性 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| UL 阻燃等级 (0.800 mm) |
HB |
-- |
|
UL 94 |
如未找到您合适的型号,或者有工程技术方面的疑问，欢迎来电来人至我公司咨询,本公司工作人员竭诚为您服务!
邓生手机:15995594155
电话:0512-53128920
传真:0512-53128921
Q Q:3378023070
邮箱:hc15995594155@126.com
Amilan PA6 CM1001G-15 高流动 玻纤15%增强 Toray Resin Company 尼龙6
Amilan PA6 CM1001G-20 高流动 玻纤20%增强 Toray Resin Company 尼龙6
Amilan PA6 CM1001R 低翘曲 矿物40%填料 Toray Resin Company 尼龙6
Amilan PA6 CM1003G30 耐磨损 玻纤30%增强 Toray Resin Company 尼龙6
Amilan PA6 CM1007 高流动 Toray Resin Company 尼龙6
Amilan PA6 CM1011G-15 玻纤15%增强 Toray Resin Company 尼龙6
Amilan PA6 CM1011G-30 玻纤30%增强 Toray Resin Company 尼龙6
Amilan PA6 CM1011G-45 玻纤45%增强 Toray Resin Company 尼龙6
Amilan PA6 CM1012G-45N 热稳定 玻纤45%增强 Toray Resin Company 尼龙6
Amilan PA6 CM1016G-30 热稳定 玻纤30%增强 Toray Resin Company 尼龙6
Amilan PA6 CM1017 树脂 Toray Resin Company 尼龙6
Amilan PA6 CM1017K 高刚性 Toray Resin Company 尼龙6
Amilan PA6 CM1017XL3 高流动 耐低温 热稳定 Toray Resin Company 尼龙6
Amilan PA6 CM1021FS 挤出级 Toray Resin Company 尼龙6
Amilan PA6 CM1021TM 单丝用 挤出级 Toray Resin Company 尼龙6
Amilan PA6 CM1023G1000 耐磨损 Toray Resin Company 尼龙6
Amilan PA6 CM1026 热稳定 Toray Resin Company 尼龙6
Amilan PA6 CM1041LO 挤出级 Toray Resin Company 尼龙6
Amilan PA6 CM1046 吹塑成型 Toray Resin Company 尼龙6
Amilan PA6 CM1046K4 吹塑成型 高粘度 高抗撞击 Toray Resin Company 尼龙6
Amilan PA6 CM1056 高粘度 高抗撞击 吹塑成型 Toray Resin Company 尼龙6
Amilan PA6 CM1056K48 高粘度 吹塑成型 玻纤20%增强 Toray Resin Company 尼龙6
Amilan PA6 CM1061 高粘度 吹塑成型 Toray Resin Company 尼龙6
Amilan PA6 EA1R21G33 玻纤33%增强 Toray Resin Company 尼龙6
Amilan PA6 U121 高抗撞击 Toray Resin Company 尼龙6
Amilan PA6 U127GX07 高抗撞击 玻纤35%增强 Toray Resin Company 尼龙6
Amilan PA6 U141 超高抗冲击 Toray Resin Company 尼龙6