Ashley Polymers Ashlene® 830LS-33G Nylon 6, 33% Glass Reinforced
Polymer,Thermoplastic,Nylon,Nylon 6,Nylon 6, 30% Glass Fiber Filled
Ashley Polymers
产品说明:
A 33% glass fiber reinforced and heat stabilized Nylon 6 designed to provide a high flexural modulus and good dimensional stability while maintaining the ease of processing associated with Nylon 6 type materials.
Data provided by the manufacturer
Ashley Polymers Ashlene® 830LS-33G Nylon 6, 33% Glass Reinforced 物性表
| 物理性能 |
额定值 (公制) |
额定值 (英制) |
测试方法 |
| 密度 |
1.37 g/cc |
0.0495 lb/in3 |
ASTM D792 |
| 吸水率 |
1.1 % |
1.1 % |
ASTM D570 |
| 线性成型收缩率 |
0.0040 cm/cm |
0.0040 in/in |
ASTM D955 |
| 机械性能 |
额定值 (公制) |
额定值 (英制) |
测试方法 |
| 洛氏硬度（R 级） |
120 |
120 |
ASTM D785 |
| 极限抗拉强度 |
179 MPa |
26000 psi |
ATSM D638 |
| 伸长率 (断裂) |
3.0 % |
3.0 % |
ASTM D638 |
| 屈服伸长率 |
3.0 % |
3.0 % |
ASTM D638 |
| 弯曲强度 |
235 MPa |
34100 psi |
ASTM D790 |
| 弯曲模量 |
9.30 GPa |
1350 ksi |
ASTM D790 |
| 悬壁梁缺口冲击强度 |
1.12 J/cm |
2.10 ft-lb/in |
ASTM D256 |
| 热性能 |
额定值 (公制) |
额定值 (英制) |
测试方法 |
| 熔融温度 |
216 °C |
421 °F |
ASTM D3418 |
| 载荷下热变形温度(0.46 MPa) |
216 °C |
421 °F |
ASTM D648 |
| 载荷下热变形温度(1.8 MPa) |
216 °C |
421 °F |
ASTM D648 |
如未找到您合适的型号,或者有工程技术方面的疑问，欢迎来电来人至我公司咨询,本公司工作人员竭诚为您服务!
邓生手机:15995594155
电话:0512-53128920
传真:0512-53128921
Q Q:3378023070
邮箱:hc15995594155@126.com
| ALAMID? PA6 塑胶原料 尼龙 6 GF 25 HV SCHWARZ-9957 LEIS Polytechnik - polymere Werkstoffe GmbH |