Ashley Polymers Ashlene® 830L-50G Nylon 6, 50% Glass Reinforced
Polymer,Thermoplastic,Nylon,Nylon 6,Nylon 6, 50% Glass Fiber Filled
Ashley Polymers
产品说明:
Nylon 6, 50% glass reinforced resin.
Data provided by the manufacturer
Ashley Polymers Ashlene® 830L-50G Nylon 6, 50% Glass Reinforced 物性表
| 物理性能 |
额定值 (公制) |
额定值 (英制) |
测试方法 |
| 密度 |
1.56 g/cc |
0.0564 lb/in3 |
ASTM D792 |
| 吸水率 |
1.1 % |
1.1 % |
ASTM D570 |
| 线性成型收缩率 |
0.0020 cm/cm |
0.0020 in/in |
ASTM D955 |
| 机械性能 |
额定值 (公制) |
额定值 (英制) |
测试方法 |
| 极限抗拉强度 |
221 MPa |
32100 psi |
ATSM D638 |
| 伸长率 (断裂) |
1.0 % |
1.0 % |
ASTM D638 |
| 屈服伸长率 |
1.0 % |
1.0 % |
ASTM D638 |
| 弯曲强度 |
304 MPa |
44100 psi |
ASTM D790 |
| 弯曲模量 |
13.8 GPa |
2000 ksi |
ASTM D790 |
| 悬壁梁缺口冲击强度 |
1.44 J/cm |
2.70 ft-lb/in |
ASTM D256 |
| 热性能 |
额定值 (公制) |
额定值 (英制) |
测试方法 |
| 熔融温度 |
216 °C |
421 °F |
ASTM D3418 |
| 载荷下热变形温度(0.46 MPa) |
216 °C |
421 °F |
ASTM D648 |
| 载荷下热变形温度(1.8 MPa) |
210 °C |
410 °F |
ASTM D648 |
ASTM D648
载荷下热变形温度(1.8 MPa)
216 °C
421 °F
ASTM D648
如未找到您合适的型号,或者有工程技术方面的疑问，欢迎来电来人至我公司咨询,本公司工作人员竭诚为您服务!
邓生手机:15995594155
电话:0512-53128920
传真:0512-53128921
Q Q:3378023070
邮箱:hc15995594155@126.com
| ALAMID? PA6 塑胶原料 尼龙 6 GF 25 HV SCHWARZ-9957 LEIS Polytechnik - polymere Werkstoffe GmbH |